Method for selecting the composition of a construction material comprising an excavated clay soil, method and system for preparing such a construction material
The invention relates to a method ( 100 ) for selecting the composition of a construction material including an excavated clay soil, said construction material composition to include deflocculating agent and activating agent quantities adapted to the excavated clay soil, said method including a step of receiving ( 130 ) a measured value of at least one physicochemical property of an excavated clay soil, and a step of selecting ( 170 ) a deflocculating agent quantity and an activating agent quantity adapted to the excavated clay soil. In addition, the invention also relates to a method ( 200 ) for calibrating a calculation algorithm for determining the composition of a site construction material, to a construction material formed from an excavated clay soil, and to a system ( 400 ) for preparing a construction material including an excavated clay soil.
1. A construction material comprising an excavated raw clay soil and a deflocculating agent, said excavated raw clay soil comprising a mixture of different types of clays including one of the following mixtures:
illite and kaolinite,
illite and kaolinite and bentonite,
illite and bentonite,
kaolinite and bentonite,
illite and montmorillonite, or
kaolinite, illite, smectite, bentonite, chlorite, montmorillonite, muscovite, hallocyte, sepiolite, attapulgite, and vermiculite.
2. The construction material according to claim 1 , wherein the excavated raw clay soil has not undergone a combustion stage.
3. The construction material according to claim 1 , further comprising an alkaline activating agent.
4. The construction material according to claim 3 , said alkaline activating agent being a composition including a compound having a pKa greater than or equal to 10.
5. The construction material according to claim 3 , comprising:
30 to 80 wt % of the excavated raw clay soil,
1 to 10 wt % of the deflocculating agent, and
10 to 50 wt % of the alkaline activating agent.
6. The construction material according to claim 1 , said construction material comprising at least 0.1 wt. % of said deflocculating agent.
7. The construction material according to claim 1 , said construction material comprising at least 2 wt. % metal oxides.
8. The construction material according to claim 7 , said construction material having a water to dry matter weight ratio less than 1.
9. The construction material according to claim 1 , said excavated raw clay soil having particles of a size greater than 50 μm.
10. The construction material according to claim 1 , said deflocculating agent is selected among a nonionic surfactant, an anionic surfactant, a polyacrylate or an amine.
11. The construction material according to claim 1 , further comprising blast furnace slag.
12. The construction material according to claim 11 , comprising:
30 to 80 wt % of the excavated raw clay soil,
0.1 to 10 wt % of the deflocculating agent, and
5 to 10 wt % of the blast furnace slag.
13. The construction material according to claim 1 , said construction material being a construction binder.
14. The construction material according to claim 1 , said construction material being a site concrete.
15. The construction material according to claim 14 , comprising:
5 to 20 wt % of the excavated raw clay soil;
0.1 to 3 wt % of the deflocculating agent;
3 to 15 wt % of an activating agent;
25 to 45 wt % sand; and
35 to 55 wt % aggregates.
16. The construction material according to claim 14 , said site concrete including at least one of the following: plasticizers, superplasticizers, rheological retention agents or air-entraining agents.
17. The construction material according to claim 1 , further comprising at least 2 wt % silt particles.
18. The construction material according to claim 1 , the excavated raw clay soil having 80 wt % or less of particles larger than 2 μm.