Systems and methods for high strength titanium rod additive manufacturing
A method of forming a rod feedstock for titanium stir friction welding additive manufacturing may comprise: mixing a plurality of powdered metals comprising titanium, iron, vanadium, and aluminum to produce a powder blend; at least one of die pressing the powder blend to form a die pressed powder or continuously powder rolling the powder blend to form a die pressed powder; and sintering the powder blend to form a rod feedstock having a cross-sectional profile.
1. A method of titanium rod additive manufacturing, comprising:
mixing a plurality of powdered metals comprising titanium, iron, vanadium, and aluminum to produce a powder blend;
die pressing the powder blend to form a die pressed powder blend;
sintering the die pressed powder blend to form a rod feedstock having a cross-sectional profile, wherein the cross-sectional profile of the rod feedstock is a substantially square shape;
loading the rod feedstock into an additive manufacturing machine configured to deposit the rod feedstock, wherein loading the rod feedstock further comprises applying an axial force to the rod feedstock to translate the rod feedstock through an aperture of a rotating tool; and
producing, via stir friction welding, a metallic component from the rod feedstock.
2. The method of claim 1 , wherein the titanium is a titanium hydride powder.
3. The method of claim 2 , wherein the powder blend comprises between 4% and 6% by weight iron, between 0.5% to 2% by weight aluminum, and between 6% to 9% by weight vanadium.
4. The method of claim 3 , wherein the sintering is performed between 900° F. (482° C.) and 1600° F. (871° C.) and under a vacuum.
5. The method of claim 1 , wherein the die pressing is performed within a temperature range between 1652° F. (900° C.) and 2,282° F. (1,250° C.).
6. The method of claim 1 , wherein the additive manufacturing machine comprises the rotating tool having the aperture disposed therethrough.
7. The method of claim 6 , wherein the rod feedstock is fed through the aperture of the rotating tool.
8. The method of claim 1 , wherein each side length of the rod feedstock is between 0.05 inches (0.127 cm) and 0.5 inches (1.27 cm).
9. A method of forming a rod feedstock for titanium stir friction welding additive manufacturing, comprising:
mixing a plurality of powdered metals comprising titanium, iron, vanadium, and aluminum to produce a powder blend;
at least one of die pressing the powder blend to form a die pressed powder or continuously powder rolling the powder blend to form the die pressed powder; and
sintering the powder blend to form the rod feedstock having a cross-sectional profile, wherein the cross-sectional profile of the rod feedstock is a substantially square shape, wherein the cross-sectional profile of the rod feedstock corresponds to a second cross-sectional profile of a rotating tool of an additive manufacturing machine to receive the rod feedstock during a stir friction welding process.
10. The method of claim 9 , wherein the titanium is a titanium hydride powder.
11. The method of claim 10 , wherein the powder blend comprises between 4% and 6% by weight iron, between 0.5% to 2% by weight aluminum, and between 6% to 9% by weight vanadium.
12. The method of claim 9 , wherein each side length of the rod feedstock is between 0.05 inches (0.127 cm) and 0.5 inches (1.27 cm).