Apparatus and methods for selective capture of mycobacteria
A device for selectively capturing mycobacteria comprises a substrate and a capture polymer layer of poly-diallyldimethyl ammonium chloride, wherein the capture polymer layer is covalently linked onto the substrate via a UV-initiated polymerization reaction of a solution comprising diallyldimethyl ammonium chloride and a photoinitiator in water purged of dissolved oxygen, and wherein the UV exposure time is 30 seconds to 4 minutes at a power density of about 20 to about 25 mW/cm 2 . A kit can comprise the device. A microfluidic chip comprises at least a portion of at least one channel sidewall coated with a capture polymer layer of poly-diallyldimethyl ammonium chloride. A method for manufacturing the device includes plasma treating a substrate, providing a solution comprising diallyldimethyl ammonium chloride and a photoinitiator in water purged of dissolved oxygen, and coating the plasma-treated substrate via a UV-initiated polymerization reaction.
1. A method of manufacturing a device for selective capture of mycobacteria, the method comprising:
providing a substrate;
plasma treating the substrate to generate a plasma-treated substrate;
providing an aqueous monomer solution comprising diallyldimethyl ammonium chloride and a photoinitiator in water purged of dissolved oxygen;
covalently linking a capture polymer layer of poly-diallyldimethyl ammonium chloride to the plasma-treated substrate by applying the aqueous monomer solution to the plasma-treated substrate via a UV-initiated polymerization reaction,
wherein a UV exposure time is about 30 seconds to about 4 minutes at a power density of about 20 mW/cm 2 to about 25 mW/cm 2 ; and
cooling the plasma-treated substrate to about 0 degrees Celsius to about 20 degrees Celsius.
2. The method of claim 1 , wherein the plasma treating the substrate is with an oxygen plasma treatment.
3. The method of claim 1 , wherein the plasma treating the substrate is for about 5 to about 15 minutes at an RF power setting of about 20 W to about 35 W.
4. The method of claim 1 , wherein cooling the plasma-treated substrate is for about 30 seconds to about 30 minutes.
5. The method of claim 1 , wherein the aqueous monomer solution is about 7% to about 12% diallyldimethyl ammonium chloride by weight.
6. The method of claim 1 , wherein the photoinitiator is 2-Hydroxy-4′-(2-hydroxyethoxy)-2-methylpropiophenone.
7. The method of claim 1 , wherein the aqueous monomer solution additionally comprises an alcohol selected from the group consisting of: methanol, ethanol, propanol, and butanol.
8. The method of claim 1 , wherein the UV exposure time is about 50 seconds to about 1 minute and 10 seconds.
9. The method of claim 1 , wherein the substrate comprises polystyrene.
10. The method of claim 1 , wherein the substrate is a solid substrate.
11. The method of claim 1 , wherein the aqueous monomer solution is about 8.9% diallyldimethyl ammonium chloride by weight.
12. The method of claim 1 , wherein the aqueous monomer solution is about 8% to about 10% diallyldimethyl ammonium chloride by weight.
13. A method of manufacturing a device for selective capture of mycobacteria, the method comprising:
providing a substrate;
plasma treating the substrate to generate a plasma-treated substrate;
providing an aqueous monomer solution comprising diallyldimethyl ammonium chloride and a photoinitiator;
covalently linking a capture polymer layer of poly-diallyldimethyl ammonium chloride to the plasma-treated substrate by applying the aqueous monomer solution to the plasma-treated substrate via a UV-initiated polymerization reaction; and
cooling the plasma-treated substrate to about 0 degrees Celsius to about 20 degrees Celsius for about 30 seconds to about 30 minutes.
14. The method of claim 13 , wherein the plasma treating the substrate is with an oxygen plasma treatment.
15. The method of claim 13 , wherein the plasma treating the substrate is for about 5 minutes to about 15 minutes.
16. The method of claim 15 , wherein the plasma treating the substrate is at an RF power setting of about 20 W to about 35 W.
17. The method of claim 13 , wherein the aqueous monomer solution is about 7% to about 12% diallyldimethyl ammonium chloride by weight.
18. The method of claim 13 , wherein the photoinitiator is 2-Hydroxy-4′-(2-hydroxyethoxy)-2-methylpropiophenone.
19. The method of claim 13 , wherein the aqueous monomer solution additionally comprises an alcohol selected from the group consisting of: methanol, ethanol, propanol, and butanol.
20. The method of claim 13 , wherein a UV exposure time, for the UV-initiated polymerization reaction, is about 50 seconds to about 1 minute and 10 seconds.
21. The method of claim 13 , wherein the substrate comprises polystyrene.