Low density polyethylene with enhanced adhesion-to-aluminum foil by blending-in acid copolymer resins
The polymer blend includes at least 90% by weight low density polyethylene (LDPE) polymer and from 1% to 10% by weight acid copolymer based on the total weight of the polymer blend. In the polymer blend, the LDPE polymer has a melt index (I? 2 #191) from 2 g/10 min to 8 g/10 min as determined in accordance with ASTM D1238, and a molecular weight distribution from 5 to 10.5. In the polymer blend, the acid copolymer is a polymerized reaction product of: at least 60% by weight ethylene, based on the total weight of the monomers present in the ethylene acid copolymer; from 1% to 20% by weight monocarboxylic acid monomer, based on the total weight of the monomers present in the ethylene acid copolymer; and from 0 to 20% by weight alkyl acrylate monomer, based on the total weight of the monomers present in the ethylene acid copolymer.
1. A polymer blend comprising:
at least 90% by weight low density polyethylene (LDPE) polymer based on the total weight of the polymer blend, the LDPE polymer having a melt index (12) from 2 g/10 min to 5.8 g/10 min as determined in accordance with ASTM D1238 (190° C., 2.16 kg), and a molecular weight distribution (MWD) from 5 to 10.5 as determined by a conventional gel permeation chromatography method; and
from 1% to 10% by weight acid copolymer based on the total weight of the polymer blend, wherein the acid copolymer is a polymerized reaction product of:
at least 65% by weight ethylene, based on the total weight of the monomers present in the ethylene acid copolymer;
from 1% to 15% by weight monocarboxylic acid monomer, based on the total weight of the monomers present in the ethylene acid copolymer; and
from 0 to 20% by weight alkyl acrylate monomer, based on the total weight of the monomers present in the ethylene acid copolymer.
2. The polymer blend of claim 1 , wherein the LDPE polymer has a density of 0.910 g/cm 3 to 0.935 g/cm 3 and an MWD of 8.5 to 10.5.
3. The polymer blend of claim 1 , wherein the melt index of the LDPE polymer is from 2 g/10 min to 4.5 g/10 min as determined in accordance with ASTM D1238 (190° C., 2.16 kg).
4. The polymer blend of claim 1 , further comprising a linear low density polyethylene (LLDPE) polymer having a melt index (I 2 ) from 0.5 g/10 min to 30 g/10 min as determined in accordance with ASTM D1238 (190° C., 2.16 kg), and a density of 0.910 g/cm 3 to 0.935 g/cm 3 .
5. The polymer blend of claim 1 , further comprising an ethylene copolymer having a melt index (I 2 ) from 0.5 g/10 min to 30 g/10 min as determined in accordance with ASTM D1238 (190° C., 2.16 kg), wherein the ethylene copolymer comprises the reaction product of:
at least 50% by weight ethylene, based on the total weight of the monomers present in the ethylene acid copolymer; and
from 0.1% to 40% by weight comonomer, based on the total weight of the monomers present in the ethylene copolymer, the comonomer being chosen from vinyl acetate, acrylate, or carboxylic acid comonomer.
6. The polymer blend of claim 1 , wherein the polymer blend comprises from 2% to 6% by weight acid copolymer, based on the total weight of the polymer blend.
7. The polymer blend of claim 1 , wherein the acid copolymer has a melt index (I 2 ) from 2 g/10 min to 30 g/10 min as determined in accordance with ASTM D1238 (190° C., 2.16 kg).
8. The polymer blend of claim 1 , wherein the alkyl acrylate monomer comprises methyl acrylate, ethyl acrylate, n-butyl acrylate, iso-butyl acrylate, or combinations thereof; and the monocarboxylic acid monomer comprises acrylic acid, methacrylic acid, or combinations thereof.
9. The polymer blend of claim 1 , wherein the ethylene acid copolymer comprises at least 75% by weight ethylene monomer, based on the total weight of the monomers in the ethylene acid copolymer; from 2% to 6% by weight monocarboxylic acid monomer, based on the total weight of the monomers in the ethylene acid copolymer; and from 1% to 15% by wt. alkyl acrylate based on the total weight of the monomers in the ethylene acid copolymer.
10. A coated metal substrate comprising:
a metal substrate; and
a coating comprising the polymer blend of claim 1 adhered to the metal substrate.
11. The coated metal substrate of claim 10 , wherein the metal substrate comprises aluminum.
12. The coated metal substrate of claim 10 , wherein the coating has peel strength of at least 0.6 N/in as measured by ASTM F904.
13. The coated metal substrate of claim 10 , wherein the coating has peel strength of at least 1 N/in as measured by ASTM F904.
14. The coated metal substrate of claim 10 , wherein the coating has peel strength of at least 2 N/in as measured by ASTM F904.
15. An extruded article comprising the polymer blend of claim 1 .
16. The polymer blend of claim 1 , wherein the LDPE polymer has a density of 0.910 g/cm 3 to 0.920 g/cm 3 .
17. The polymer blend of claim 1 , wherein the LDPE polymer is a homopolymer.
18. The polymer blend of claim 1 , wherein the ethylene acid copolymer from 0 to 15% by weight alkyl acrylate monomer, based on the total weight of the monomers present in the ethylene acid copolymer.
19. The polymer blend of claim 1 , wherein the ethylene acid copolymer comprises at least 75% by weight ethylene monomer, based on the total weight of the monomers in the ethylene acid copolymer.
20. The polymer blend of claim 1 , wherein:
the polymer blend comprises from 2% to 6% by weight acid copolymer, based on the total weight of the polymer blend; and
the ethylene acid copolymer comprises at least 75% by weight ethylene monomer, based on the total weight of the monomers in the ethylene acid copolymer.