Thermally conductive silicone composition and production method therefor
A thermally conductive silicone composition that has high thermal conductivity and excellent workability and misalignment resistance, and contains, in specific ratios: a silicone gel cross-linked product (A); a silicone oil (B) not containing either aliphatic unsaturated bonds or SiH groups and being used as a surface treatment agent for components (C) and (D); an aluminum powder (C) including (C-1)-(C-3), (C-1) being an aluminum powder having an average particle diameter of 40-100 μm, (C-2) being an aluminum powder having an average particle diameter of at least 6 μm and less than 40 μm, and (C-3) being an aluminum powder having an average particle diameter of at least 0.4 μm and less than 6 μm; a zinc oxide powder (D) having an average particle diameter of 0.1-10 μm; and a volatile solvent (E).
1. A heat conductive silicone composition comprising
(A) a crosslinked silicone gel,
(B) a silicone oil containing neither aliphatic unsaturated bonds nor SiH groups and serving as a surface treatment agent for components (C) and (D),
(C) an aluminum powder in an amount of 800 to 2,000 parts by weight per 100 parts by weight of components (A) and (B) combined, the aluminum powder including
(C-1) an aluminum powder having an average particle size of from 40 μm to 100 μm in an amount of 30 to 70% by weight of component (C),
(C-2) an aluminum powder having an average particle size of from 6 μm to less than 40 μm in an amount of 10 to 60% by weight of component (C), and (C-3) an aluminum powder having an average particle size of from 0.4 um to less than 6 um in an amount of 10 to 60% by weight of component (C),
(D) a zinc oxide powder having an average particle size of 0.1 to 10 μm in an amount of 50 to 500 parts by weight per 100 parts by weight of components (A) and (B) combined, and
(E) a volatile solvent in an amount of 10 to 300 parts by weight per 100 parts by weight of components (A) and (B) combined.
2. The heat conductive silicone composition of claim 1 wherein component (B) contains (B-1) a silicone oil in the form of a one end hydrolyzable organopolysiloxane having the general formula (1):
wherein R 1 is each independently a C 1 -C 6 alkyl group, R 2 is at least one group selected from C 1 -C 18 aliphatic unsaturation-free, unsubstituted or substituted monovalent hydrocarbon groups, and a is an integer of 5 to 120, and component (B) is blended in an amount of 10 to 90% by weight based on the total weight of components (A) and (B).
3. The heat conductive silicone composition of claim 1 wherein component (A) contains a crosslinked silicone gel composed of:
(F) an organopolysiloxane containing at least one silicon-bonded alkenyl group per molecule, represented by the average compositional formula (2):
R 3 b R 4 c SiO (4-b-c)/2 (2)
wherein R 3 is an alkenyl group, R 4 is an aliphatic unsaturation-free, unsubstituted or substituted monovalent hydrocarbon group, b is a number of 0.0001 to 0.2, c is a number of 1.7 to 2.2, and b+c is a number of 1.9 to 2.4, and
(G) an organohydrogenpolysiloxane containing at least 4 silicon-bonded hydrogen atoms at non-terminal positions of the molecular chain per molecule, and meeting the formula (3):
0.1<α/β (3)
wherein α is the number of silicon-bonded hydrogen atoms at non-terminal positions of the molecular chain and β is the total number of silicon atoms in component (G).
4. The heat conductive silicone composition of claim 1 wherein component (B) further contains (B-2) a non-functional liquid silicone oil having a kinematic viscosity of 10 to 500,000 mm 2 /s at 25° C., in an amount of 10 to 70% by weight of component (B).
5. The heat conductive silicone composition of claim 1 wherein component (E) is an isoparaffin base solvent having a boiling point of 80 to 360° C.
6. A method of preparing a heat conductive silicone composition comprising the step of mixing the following:
(A) a crosslinked silicone gel,
(B) a silicone oil containing neither aliphatic unsaturated bonds nor SiH groups and serving as a surface treatment agent for components (C) and (D),
(C) an aluminum powder in an amount of 800 to 2,000 parts by weight per 100 parts by weight of components (A) and (B) combined, the aluminum powder including
(C-1) an aluminum powder having an average particle size of from 40 μm to 100 μm in an amount of 30 to 70% by weight of component (C),
(C-2) an aluminum powder having an average particle size of from 6 μm to less than 40 μm in an amount of 10 to 60% by weight of component (C), and
(C-3) an aluminum powder having an average particle size of from 0.4 μm to less than 6 μm in an amount of 10 to 60% by weight of component (C),
(D) a zinc oxide powder having an average particle size of 0.1 to 10 μm in an amount of 50 to 500 parts by weight per 100 parts by weight of components (A) and (B) combined, and
(E) a volatile solvent in an amount of 10 to 300 parts by weight per 100 parts by weight of components (A) and (B) combined.