Method of producing conducting polymer network-enabled particulates of anode active material particles for lithium-ion batteries
Provided is a method of producing multi-functional particulates of graphene-protected conducting polymer gel network-encapsulated anode particles for a lithium battery, said method comprising: a) Dispersing a plurality of primary particles of an anode active material, having a diameter or thickness from 0.5 nm to 20 μm, and multiple graphene sheets into a precursor to a conducting polymer gel network to form a suspension; and b) Forming said suspension into micro-droplets and, concurrently or sequentially, polymerizing and/or crosslinking said precursor to form said multi-functional particulates. The conducting polymer gel network comprises a polyaniline hydrogel, polypyrrole hydrogel, or polythiophene hydrogel in a dehydrated state.
1. A method of producing multi-functional particulates of graphene-protected conducting polymer gel network-encapsulated anode particles for a lithium battery, said method comprising:
a) Dispersing a plurality of primary particles of an anode active material, having a diameter or thickness from 0.5 nm to 20 μm, and multiple graphene sheets into a precursor to a conducting polymer gel network to form a suspension; and
b) Forming said suspension into micro-droplets and, concurrently or sequentially, polymerizing and/or crosslinking said precursor to form said multi-functional particulates;
wherein said conducting polymer gel network comprises a polyaniline hydrogel, polypyrrole hydrogel, or polythiophene hydrogel in a dehydrated state.
2. The method of claim 1 , wherein said conducting polymer gel network comprises a conjugated polymer selected from polyacetylene, polythiophene, poly(3-alkylthiophenes), polypyrrole, polyaniline, poly(isothianaphthene), poly(3,4-ethylenedioxythiophene), alkoxy-substituted poly(p-phenylene vinylene), poly(2,5-bis(cholestanoxy)phenylene vinylene), poly(p-phenylene vinylene), poly(2,5-dialkoxy)paraphenylene vinylene, poly[(1,4-phenylene-1,2-diphenylvinylene)], poly(3′,7′-dimethyloctyloxy phenylene vinylene), polyparaphenylene, polyparaphenylene, polyparaphenylene sulphide, polyheptadiyne, poly(3-hexylthiophene), poly(3-octylthiophene), poly(3-cyclohexylthiophene), poly(3-methyl-4-cyclohexylthiophene), poly(2,5-dialkoxy-1,4-phenyleneethynylene), poly(2-decyloxy-1,4-phenylene), poly(9,9-dioctylfluorene), polyquinoline, a derivative thereof, a copolymer thereof, a sulfonated version thereof, or a combination thereof.
3. The method of claim 1 , where said step of forming said suspension into micro-droplets includes operating a procedure selected from pan-coating, air-suspension coating, centrifugal extrusion, vibration-nozzle encapsulation, spray-drying, coacervation-phase separation, interfacial polycondensation or interfacial cross-linking, in-situ polymerization, matrix polymerization, or a combination thereof.
4. The method of claim 1 , wherein said anode active material primary particles contain particles pre-coated with a layer of a conductive material selected from a carbon, pitch, carbonized resin, conductive polymer, conductive organic material, metal coating, metal oxide shell, graphene, or a combination thereof.
5. The method of claim 1 , further comprising a step of incorporating said multi-functional particulates into a battery anode electrode.