Low electrical resistance microporous battery separator membranes, separators, cells, batteries, and related methods
Microporous battery separator membranes, separators, batteries including such membranes, separators are provided. A battery separator for a secondary or rechargeable lithium battery may have low Electrical resistance of less than 0.95 ohm-cm 2 . The inventive battery separator membrane may provide a means to achieve an improved level of battery performance in a rechargeable or secondary lithium battery based on a possibly synergistic combination of low Electrical resistance, low Gurley, low tortuosity, and/or a unique trapezoid shaped pore. Certain multilayer embodiments (by way of example only, a trilayer membrane made of two polypropylene layers with a polyethylene layer in between), the inventive microporous membrane or battery separator may have excellent onset and rate of thermal shutdown performance.
1. A porous polyolefin membrane, comprising:
a dry process microporous polyolefin membrane having an electrical resistance less than 0.95 ohm-cm 2 ,
having a Gurley less than 500 sec/100 cc,
having a tortuosity less than 1.5, and
wherein said microporous polyolefin membrane has a puncture strength of at least 250 gf.
2. The porous polyolefin membrane of claim 1 wherein the microporous polyolefin membrane has an electrical resistance less than 0.8 ohm-cm 2 ,
having a Gurley less than 150 sec/100 cc,
having a tortuosity less than 1.3,
having a puncture strength of over 250 gf, and/or
wherein said microporous polyolefin membrane comprises polypropylene, polyethylene, mixtures thereof, and/or co-polymers thereof.
3. The porous polyolefin membrane of claim 1 where said microporous polyolefin membrane is a monolayer membrane or a multilayer membrane with a thermal shutdown function.
4. The porous polyolefin membrane of claim 1 where said microporous polyolefin membrane is a multilayer membrane consisting of a trilayer of polypropylene/polyethylene/polypropylene.
5. The porous polyolefin membrane of claim 1 wherein said microporous polyolefin membrane has a thickness less than 25 μm.
6. The porous polyolefin membrane of claim 5 wherein said microporous polyolefin membrane has pores with a non-round, trapezoid shape on each surface of said membrane.
7. The porous polyolefin membrane of claim 1 wherein the porous polyolefin membrane is made by a process comprising:
extruding a polypropylene which has a melt flow index less than 1.0 g/10 minutes to form a monolayer nonporous precursor membrane and,
machine direction stretching the nonporous polypropylene precursor membrane to form a semi-porous intermediate membrane having a puncture strength>350 gf and TD elongation>600%,
transverse direction stretching the semi-porous intermediate membrane using a stretch ratio of 15 to 400% to form the porous polyolefin membrane.
8. The porous polyolefin membrane of claim 7 , wherein said semi-porous intermediate membrane is transverse stretched at a temperature of 100 to 130 deg C., wherein said semi-porous intermediate membrane is transverse stretched at a temperature of 100 to 130 deg C. at a speed of 100 ft/minute, wherein said semi-porous intermediate membrane is thermally relaxed at 120 to 140 deg C., and/or wherein said semi-porous intermediate membrane is heat treated at a temperature of 60 to 100 deg C. for 8 hours to 3 days.
9. The porous polyolefin membrane of claim 1 wherein the microporous polyolefin membrane is a microporous trilayer membrane made by a process comprising:
extruding a polyethylene which has a melt flow index less than 1.0 g/10 minutes to form a monolayer nonporous polyethylene precursor membrane and,
extruding a polypropylene which has a melt flow index less than 1.0 g/10 minutes to form a monolayer nonporous polypropylene precursor membrane and,
laminating two plies of polypropylene precursor membrane as outer plies (layers) sandwiching one inner ply (layer) of polyethylene precursor membrane to form a trilayer polypropylene/polyethylene/polypropylene nonporous precursor,
machine direction stretching a nonporous polypropylene/polyethylene/polypropylene precursor membrane to form a semi-porous intermediate membrane having a puncture strength>350 gf and TD elongation>600%,
transverse direction stretching a semi-porous intermediate membrane using a stretch ratio of 15 to 400% to form a microporous trilayer membrane.
10. The porous polyolefin membrane of claim 9 , wherein said semi-porous intermediate membrane is transverse stretched at a temperature of 100 to 130 deg C., formed wherein said semi-porous intermediate membrane is transverse stretched at a temperature of 100 to 130 deg C. at a speed of 100 ft/minute, wherein the semi-porous intermediate membrane is thermally relaxed at 120 to 140 deg C., and/or wherein the semi-porous intermediate membrane is heat treated at a temperature of 60 to 100 deg C. for 8 hours to 3 days.
11. A battery separator comprising the porous polyolefin membrane of claim 1 .
12. A battery separator comprising the porous polyolefin membrane of claim 7 .
13. A battery separator comprising the porous polyolefin membrane of claim 9 .
14. A lithium battery comprising the battery separator of claim 11 .
15. A lithium battery comprising the battery separator of claim 12 .
16. A lithium battery comprising the battery separator of claim 13 .
17. A dry process microporous polyolefin membrane battery separator having a synergistic combination of electrical resistance less than 0.95 ohm-cm 2 , Gurley less than 150 seconds/100 cc, tortuosity of less than 1.2, and having a porous structure which resembles a substantially knitted structure where a polymer crystalline lamellae regions resemble small islands connected by a 3-D array of vertically and diagonally elongated fibrillar structures, and/or with pores having a non-round pore shape.