US 12,278,366 · App. 17/413,160 · Granted Apr 15, 2025

Lithium cobalt aluminum oxide positive electrode active material including aluminum-containing coating film and secondary battery

Inventors: Jyo Saito (Kanagawa, JP); Mayumi Mikami (Kanagawa, JP); Yohei Momma (Kanagawa, JP); Teruaki Ochiai (Kanagawa, JP); Tatsuyoshi Takahashi (Kanagawa, JP); Kazuhei Narita (Tokyo, JP)
Assignee: Semiconductor Energy Laboratory Co., Ltd.
H01M4/525H01M4/366H01M10/0525H01M10/0569H01M2004/021H01M2004/028
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,278,366
App. No.
17/413,160
Granted
Apr 15, 2025
Kind
B2
Abstract

A positive electrode active material that has high capacity and excellent charge and discharge cycle performance for a secondary battery is provided. A positive electrode active material that inhibits a decrease in capacity in charge and discharge cycles is provided. A high-capacity secondary battery is provided. A secondary battery with excellent charge and discharge characteristics is provided. A highly safe or reliable secondary battery is provided. A positive electrode active material contains lithium, cobalt, oxygen, and aluminum and has a crystal structure belonging to a space group R-3m when Rietveld analysis is performed on a pattern obtained by powder X-ray diffraction. In analysis by X-ray photoelectron spectroscopy, the number of aluminum atoms is less than or equal to 0.2 times the number of cobalt atoms.

Claims (47)

1. A positive electrode active material comprising:

a first particle group and a second particle group,

wherein the positive electrode active material has a crystal structure belonging to a space group R-3m,

wherein the crystal structure is estimated by Rietveld analysis of a pattern obtained by powder X-ray diffraction using a CuKα1 ray,

wherein the positive electrode active material comprises lithium cobalt oxide, magnesium, aluminum, and nickel,

wherein, in X-ray photoelectron spectroscopy of the positive electrode active material, a number of aluminum atoms is less than a number of magnesium atoms and greater than a number of nickel atoms,

wherein a particle size distribution of the first particle group has a first local maximum peak and a particle size distribution of the second particle group has a second local maximum peak,

wherein the first local maximum peak has a local maximum value at greater than or equal to 9 μm and less than or equal to 25 μm,

wherein the second local maximum peak has a local maximum value at greater than or equal to 0.1 μm and less than 9 μm,

wherein the first particle group comprises a first positive electrode active material particle comprising lithium cobalt oxide, magnesium, aluminum, and nickel,

wherein the second particle group comprises a second positive electrode active material particle comprising lithium cobalt oxide, aluminum, and nickel,

wherein, in any one of ICP-MS, GD-MS, and elementary analysis of atomic absorption, an atomic ratio of magnesium to cobalt in the first particle group is greater than or equal to 0.001 and less than or equal to 0.06, and

wherein the atomic ratio of magnesium to cobalt in the first particle group is higher than an atomic ratio of magnesium to cobalt in the second particle group.

2. The positive electrode active material according to claim 1 ,

wherein the particle size distribution is measured with a laser diffraction particle size distribution measurement tool.

3. The positive electrode active material according to claim 1 , wherein in the X-ray photoelectron spectroscopy of the positive electrode active material, the number of magnesium atoms is greater than or equal to 0.4 times and less than or equal to 1.5 times a number of cobalt atoms.

4. The positive electrode active material according to claim 3 ,

wherein in the X-ray photoelectron spectroscopy of the positive electrode active material, an extraction angle is greater than or equal to 40° and less than or equal to 50°.

5. A positive electrode comprising:

a current collector; and

a positive electrode active material layer over the current collector,

wherein the positive electrode active material layer comprises the positive electrode active material according to claim 1 , and

wherein a density of the positive electrode active material layer is greater than or equal to 3.8 g/cm 3 and less than or equal to 4.5 g/cm 3 .

6. A secondary battery comprising:

a positive electrode comprising the positive electrode active material according to claim 1 ;

a negative electrode; and

an electrolyte solution,

wherein, when charge and discharge are repeatedly performed from a first cycle to a 50th cycle, a second discharge capacity obtained by the discharge in the 50th cycle is greater than or equal to 90% of a first discharge capacity obtained by the discharge in the first cycle.

7. The secondary battery according to claim 6 ,

wherein the charge is performed under CCCV condition,

wherein current of a CC charge is higher than or equal to 0.01 C and lower than or equal to 1.0 C,

wherein upper limit voltage of the CC charge is higher than or equal to 4.55 V with reference to Li/Li + ,

wherein a termination current of a CV charge is higher than or equal to 0.001 C,

wherein the discharge is performed under CC condition,

wherein current of a CC discharge is higher than or equal to 0.05 C and lower than or equal to 2.0 C, and

wherein measurement temperature is higher than or equal to 15° C. and lower than or equal to 55° C.

8. A secondary battery comprising:

a positive electrode comprising the positive electrode active material according to claim 1 ,

wherein a lithium metal is used for a counter electrode,

wherein, when charge and discharge are repeatedly performed from a first cycle to a 50th cycle, a second discharge capacity obtained by the discharge in the 50th cycle is greater than or equal to 90% of a first discharge capacity obtained by the discharge in the first cycle,

wherein the charge is performed under CCCV condition,

wherein current of a CC charge is higher than or equal to 0.01 C and lower than or equal to 1.0 C,

wherein upper limit voltage of the CC charge is higher than or equal to 4.55 V with reference to Li/Li + ,

wherein a termination current of a CV charge is higher than or equal to 0.001 C,

wherein the discharge is performed under CC condition,

wherein current of a CC discharge is higher than or equal to 0.05 C and lower than or equal to 2.0 C, and

wherein measurement temperature is higher than or equal to 15° C. and lower than or equal to 55° C.

Assignments (1)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jun 11, 2021
From: SAITO, JYO; MIKAMI, MAYUMI; MOMMA, YOHEI; OCHIAI, TERUAKI; TAKAHASHI, TATSUYOSHI; NARITA, KAZUHEI
To: SEMICONDUCTOR ENERGY LABORATORY CO., LTD.
Reel/Frame 056515/0665 →
Priority Claims (2)
JP 2018-235792 · Dec 17, 2018 · national
JP 2018-235801 · Dec 17, 2018 · national
Continuity (1)
Related Publication 20220052335A1 · Feb 17, 2022
References Cited (87)
US 4302518A · Goodenough et al. · 1981 [cited by applicant]
US 4668595A · Yoshino et al. · 1987 [cited by applicant]
US 5783333A · Mayer · 1998 [cited by applicant]
US 5871866A · Barker et al. · 1999 [cited by applicant]
US 5910382A · Goodenough et al. · 1999 [cited by applicant]
US 6085015A · Armand et al. · 2000 [cited by applicant]
US 6514640B1 · Armand et al. · 2003 [cited by applicant]
US 6737195B2 · Kweon et al. · 2004 [cited by applicant]
US 6974601B2 · Kweon et al. · 2005 [cited by applicant]
US 7309546B2 · Kweon et al. · 2007 [cited by applicant]
US RE43276E · Kweon et al. · 2012 [cited by applicant]
US 9184439B2 · Miyoshi et al. · 2015 [cited by applicant]
US 9899664B2 · Yamaki et al. · 2018 [cited by applicant]
US 20010010807A1 · Matsubara · 2001 [cited by applicant]
US 20020055042A1 · Kweon et al. · 2002 [cited by applicant]
US 20020110736A1 · Kweon et al. · 2002 [cited by applicant]
US 20020195591A1 · Ravet et al. · 2002 [cited by applicant]
US 20030104279A1 · Miyazaki et al. · 2003 [cited by applicant]
US 20030138699A1 · Kweon et al. · 2003 [cited by applicant]
US 20040142241A1 · Nagayama · 2004 [cited by applicant]
US 20050271944A1 · Suhara · 2005 [cited by examiner]
US 20060051671A1 · Thackeray et al. · 2006 [cited by applicant]
US 20060263690A1 · Suhara et al. · 2006 [cited by applicant]
US 20070117014A1 · Saito et al. · 2007 [cited by applicant]
US 20070190421A1 · Sato · 2007 [cited by examiner]
US 20080241693A1 · Fukuchi et al. · 2008 [cited by applicant]
US 20090087362A1 · Sun et al. · 2009 [cited by applicant]
US 20090104532A1 · Hosoya · 2009 [cited by applicant]
US 20100086854A1 · Kumar et al. · 2010 [cited by applicant]
US 20100247986A1 · Toyama et al. · 2010 [cited by applicant]
US 20110227000A1 · Ruoff et al. · 2011 [cited by applicant]
US 20120258370A1 · Miyoshi et al. · 2012 [cited by applicant]
US 20120315550A1 · Liu et al. · 2012 [cited by applicant]
US 20130052534A1 · Fujiki et al. · 2013 [cited by applicant]
US 20130323596A1 · Morita et al. · 2013 [cited by applicant]
US 20140377659A1 · Oljaca · 2014 [cited by examiner]
US 20150357641A1 · Sugie et al. · 2015 [cited by applicant]
US 20160006032A1 · Paulsen · 2016 [cited by examiner]
US 20160013478A1 · Satow et al. · 2016 [cited by applicant]
US 20160276659A1 · Choi et al. · 2016 [cited by applicant]
US 20170040594A1 · Yamaki et al. · 2017 [cited by applicant]
US 20180013130A1 · Ochiai et al. · 2018 [cited by applicant]
US 20180145317A1 · Momma et al. · 2018 [cited by applicant]
US 20180145368A1 · Ochiai et al. · 2018 [cited by applicant]
US 20200176770A1 · Takahashi et al. · 2020 [cited by applicant]
US 20210083281A1 · Mikami et al. · 2021 [cited by applicant]
CN 001434527A · 2003 [cited by applicant]
CN 100426570C · 2008 [cited by applicant]
CN 101562248A · 2009 [cited by applicant]
CN 105655554A · 2016 [cited by applicant]
CN 106450272A · 2017 [cited by applicant]
EP 3503252A1 · 2019 [cited by examiner]
JP 08037007A · 1996 [cited by applicant]
JP 2000203842A · 2000 [cited by applicant]
JP 2001291518A · 2001 [cited by applicant]
JP 2002216760A · 2002 [cited by applicant]
JP 2003217572A · 2003 [cited by applicant]
JP 2006261132A · 2006 [cited by applicant]
JP 2010080407A · 2010 [cited by applicant]
JP 2015069958A · 2015 [cited by applicant]
JP 2015099722A · 2015 [cited by applicant]
JP 2016091633A · 2016 [cited by applicant]
JP 2017033817A · 2017 [cited by applicant]
KR 20010091887A · 2001 [cited by applicant]
KR 20030063930A · 2003 [cited by applicant]
KR 20130124610A · 2013 [cited by applicant]
KR 20140073048A · 2014 [cited by applicant]
KR 20170016782A · 2017 [cited by applicant]
KR 20180089698A · 2018 [cited by applicant]
WO WO2011077654 · 2011 [cited by applicant]
WO WO2011141486 · 2011 [cited by applicant]
WO WO2017046723A1 · 2017 [cited by examiner]
Taiwanese Office Action (Application No. 108144515) dated Aug. 30, 2023. [cited by applicant]
International Search Report (Application No. PCT/IB2019/060418) dated Feb. 18, 2020. [cited by applicant]
Written Opinion (Application No. PCT/IB2019/060418) dated Feb. 18, 2020. [cited by applicant]
Okumura.T et al., “Correlation of lithium ion distribution and X-ray absorption near-edge structure in O3- and O2-lithium cobalt oxides from first-principle calculation”, Journal of Materials Chemistry, 2012, vol. 22, p… [cited by applicant]
Motohashi.T et al., “Electronic phase diagram of the layered cobalt oxide system LixCoO2 (0.0≤x≤1.0)”, Phys. Rev. B (Physical Review. B), Oct. 9, 2009, vol. 80, No. 16, pp. 165114-1-165114-9. [cited by applicant]
Chen.Z et al., “Staging Phase Transitions in LixCoO2”, J. Electrochem. Soc. (Journal of The Electrochemical Society), 2002, vol. 149, No. 12, pp. A1604-A1609. [cited by applicant]
Counts. W et al., “Fluoride Model Systems: II, The Binary Systems CaF2—BeF2, MgF2—BeF2, and LiF—MgF2”, J. Am. Ceram. Soc. (Journal of The American Ceramic Society), 1953, vol. 36, No. 1, pp. 12-17. [cited by applicant]
Belsky.A et al., “New developments in the Inorganic Crystal Structure Database (ICSD): Accessibility in support of materials research and design.”, Acta. Cryst.(Acta Crystallographica Section B), Jun. 1, 2002, vol. B58,… [cited by applicant]
Dudarev.S et al., “Electron-energy-loss spectra and the structural stability of nickel oxide: An LSDA+U study”, Phys. Rev. B (Physical Review. B), Jan. 15, 1998, vol. 57, No. 3, pp. 1505-1509. [cited by applicant]
Zhou.F et al., “First-principles prediction of redox potentials in transition-metal compounds with LDA+U”, Phys. Rev. B (Physical Review. B), Dec. 15, 2004, vol. 70, No. 23, pp. 235121-1-235121-8. [cited by applicant]
Todoriki.H et al., “High performance lithium ion battery using Graphene Net electrode”, 222nd ECS Meeting Abstract, Oct. 7, 2012, p. 1014, ECS. [cited by applicant]
Dreyer.D et al., “The Chemistry of Graphene Oxide”, Chemical Society Reviews, Nov. 3, 2009, vol. 39, No. 1, pp. 228-240. [cited by applicant]
Nitta.N et al., “Li-ion battery materials: present and future”, Materials Today, Jun. 1, 2015, vol. 18, No. 5, pp. 252-264. [cited by applicant]
Hong.L et al., “Research on Advanced Materials for Li-ion Batteries”, Adv. Mater. (Advanced Materials), Dec. 3, 2009, vol. 21, No. 45, pp. 4593-4607. [cited by applicant]
Wang. Y et al., “Developments in Nanostructured Cathode Materials for High-Performance Lithium-Ion Batteries”, Adv. Mater. (Advanced Materials), Jun. 18, 2008, vol. 20, No. 12, pp. 2251-2269. [cited by applicant]