Granted Patent B2

US 12,281,374 · App. 15/733,312 · Granted Apr 22, 2025

Inventor: Henning Fehrmann (Hamburg, DE)

Assignee: Fehrmann Alloys GmbH & Co. KG

C22C21/06B22F10/25B22F10/28B22F10/34B22F10/64B22F10/66C22C21/08B22F2301/052B33Y10/00B33Y70/00B33Y80/00

Abstract

Claims (38)

1. A method for the additive manufacture of a workpiece, comprising:

a. providing a raw aluminum;

b. heating the raw aluminum to a temperature in a range of from 650 to 800° C.;

c. adding Mg and Be to result in a raw alloy;

d. optionally degassing the raw alloy;

e. adding Ti and B to an optionally degassed raw alloy to prepare the aluminum alloy

f. setting a layer of aluminum powder comprising the aluminum alloy;

g. selectively melting the aluminum powder by using at least one laser beam;

h. iterating steps f. and g. until the workpiece is finished,

wherein the aluminum alloy comprises:

A. from 9 to 14% by mass of magnesium (Mg);

B. from 0.15 to 1% by mass of titanium (Ti);

C. from 0.0001 to 0.1% by mass of manganese (Mn);

D. from 0 to 0.1% by mass of iron (Fe);

E. from 0.001 to 0.1% by mass of beryllium (Be);

F. from 0.0009 to 0.2% by mass of boron (B);

G. from 0 to 1% by mass of silicon (Si);

H. from 0 to 0.01% by mass of copper (Cu);

I. from 0 to 0.01% by mass of zinc (Zn);

J. from 0 to 0.05% by mass of scandium (Sc); and

K. from 0 to 0.05% by mass of inevitable impurities;

with the balance being aluminum (Al);

wherein each is in relation to a total mass of the aluminum alloy, and wherein A.-K. and Al of the aluminum alloy add up to a total of 100% by mass.

2. The method according to claim 1 , wherein the method further comprises

i. treating the workpiece by blasting, machining, heat and/or other treatments.

3. The method according to claim 2 , wherein the workpiece is heat treated in step i.

by heating the workpiece at a temperature of at least 380° C.,

for a period of at least 10 minutes to less than 24 hours, and

then cooled in air at ambient temperature.

4. The method according to claim 1 , wherein the additive manufacture is selected from the group consisting of selective laser sintering (SLS), selective laser melting (SLM), direct metal laser sintering, and laser metal deposition (LMD).

5. The method according to claim 4 , wherein the additive manufacture is selective laser sintering or selective laser melting.

6. The method according to claim 1 , wherein the aluminum alloy comprises Mg in an amount of from 9.1 to 13.9% by mass.

7. The method according to claim 1 , wherein the aluminum alloy comprises Ti in an amount of from 0.2 to 0.9% by mass.

8. The method according to claim 1 , wherein the aluminum alloy comprises Mn in an amount of 0.0005 to 0.09% by mass.

9. The method according to claim 1 , wherein the aluminum alloy comprises Fe in an amount of 0.01 to 0.09% by mass.

10. The method according to claim 1 , wherein the aluminum alloy comprises Be in an amount of from 0.002 to 0.09% by mass.

11. The method according to claim 1 , wherein the aluminum alloy comprises B in an amount of from 0.001 to 0.15% by mass.

12. The method according to claim 1 , wherein the aluminum alloy comprises Si in an amount of 0.01 to 0.5% by mass.