Tool-less method for making molds, cores, and temporary tools
A tool-less method for making molds, cores, and temporary tools includes the steps of providing a volumetric build system, making a CAD model of a three-dimensional object, selecting a build material including an untreated sand, selecting a binder comprising a polymeric carbohydrate, and applying, by the volumetric build system, the binder onto the build material to three dimensionally print the object, wherein the object is adapted for being a mold, a core, or a temporary tool.
1. A method for producing bonded sand shapes adapted to be used as molds and cores for a metal casting process, said method comprising the steps of:
providing an additive volumetric build system having a print bed;
making a CAD model of a three-dimensional object;
selecting a build material comprising untreated sand;
selecting a single component binder consisting of starch and an aqueous liquid carrier comprising water in a range of about 40 weight percent to 80 weight percent and forming a binder composition;
applying the untreated sand in layers repeatedly by the additive volumetric build system by printing in both directions a length of the print bed;
applying the binder composition to selective areas of the layers of the untreated sand without precoating the untreated sand to form a solid shape of the object;
heating the applied binder composition with an infrared device or microwave device;
dehydrating the applied binder composition to form a solid bond between grains of the applied binder composition sand; and
removing unbonded and untreated sand from around the bonded sand shape.
2. A method as set forth in claim 1 including the step of using at least one inkjet printhead to apply the binder.
3. A method as set forth in claim 2 including the step of using an anti-static bar to keep the sand off of a print head nozzle plate of the printhead.
4. A method as set forth in claim 1 including the step of using electro-magnetic radiation in the infra-red range to heat, dehydrate, and harden the binder.
5. A method as set forth in claim 1 including the step of using electro-magnetic radiation in the microwave range to heat, dehydrate and harden the binder.
6. A method as set forth in claim 1 including the step of evacuating water vapor from the print bed.
7. A method as set forth in claim 1 including the step of striking off/compacting the sand.
8. A method according to claim 1 , wherein the binder composition is a solution of the starch dissolved in the water.
9. A method according to claim 1 , wherein the infrared device produces infrared light in mid-range infrared wavelengths.
10. A method according to claim 1 , wherein the recovered, partially burned, post casting sand is cleaned of residual binder by water washing, thermal treatment, or a combination thereof.
11. A method according to claim 1 , wherein the sand contains additives adapted for production of the metal castings.
12. A method according to claim 1 , wherein the binder composition is a solution of the starch chosen from at least one of starches derived from corn, potato, rice, wheat, or cassava root.
13. A method according to claim 12 , wherein the starch derived from corn is dissolved in the water.
14. A method according to claim 1 , wherein the binder composition includes at least one of a surfactant, a biocide, and a colorant.
15. A method according to claim 1 , wherein the partially burned, post casting sand is heated to a temperature above 750° F. in order to substantially remove any residual binder.
16. A method according to claim 15 , wherein the heated sand becomes thermally reclaimed sand and is used in place of new sand adapted to produce the molds and cores for making the metal castings.
17. A method as set forth in claim 1 including the step of removing the bonded sand shape from the additive volumetric build system and using the bonded sand shape as at least one of molds and cores without post curing to make metal castings.
18. A method as set forth in claim 1 wherein the microwave device produces microwaves with a wavelength between 0.915 GHz and 5.86 GHz.
19. A method for producing bonded sand shapes adapted to be used as molds and cores for a metal casting process comprising the steps of:
obtaining a representation of a three-dimensional object;
selecting a build material comprising untreated sand;
selecting a single component binder consisting of starch and an aqueous liquid carrier comprising water in a range of about 40 weight percent to 80 weight percent and forming a binder composition;
using the representation of the object, applying the untreated sand in layers, and applying the binder composition to selective areas of the layers of the untreated sand without precoating the untreated sand to form a solid shape of the object;
heating the applied binder composition with an infrared device or microwave device;
dehydrating the applied binder composition to form a solid bond between grains of the applied binder composition sand; and
removing loose, unbonded and untreated sand from around the bonded sand shape.
20. A method as set forth in claim 19 including the step of using a plurality of inkjet printheads to apply the binder.
21. A method as set forth in claim 20 including the step of using an anti-static bar to keep the sand off of a print head nozzle plate of the printheads.
22. A method as set forth in claim 19 including the step of using electro-magnetic radiation in the infra-red range to heat, dehydrate and harden the binder.
23. A method as set forth in claim 19 including the step of using electro-magnetic radiation in the microwave range to heat, dehydrate and harden the binder.
24. A method as set forth in claim 19 including the step of evacuating water vapor from the print bed.
25. A method as set forth in claim 19 including the step of striking off/compacting the sand.
26. A method for producing bonded sand shapes adapted for use as molds and cores for a metal casting process, said method comprising the steps of:
applying untreated sand to form layers repeatedly made by a CAD driven additive system having a print bed and printing in both directions a length of the print bed;
applying a single component binder consisting of starch and an aqueous liquid carrier comprising water in a range of about 40 weight percent to 80 weight percent and forming a binder composition to selective areas of each of the layers where the untreated sand is to form a solid shape without precoating the untreated sand;
passing the binder composition through a plurality of inkjet printheads that cover a width of the print bed width;
heating the applied binder composition with an infrared device or microwave device;
dehydrating the applied binder composition to form a solid bond between grains of the applied binder composition sand;
removing the loose, unbonded and untreated sand from around the bonded sand shape;
removing the bonded sand shape from the additive system and using the hardened sand shapes as molds, and/or cores, without post curing, to make metal castings.