Polyamide composition and a tubular or pipe multilayer structure comprising the same
Described herein is a polyamide composition and a tubular or pipe multilayer structure including the same.
1. A polyamide composition, comprising:
(a) a polyamide copolymer obtained by reacting
(i) ε-caprolactam, and
(ii) a mixture of hexamethylenediamine with a diacid comprising at least 9 carbon atoms,
wherein the weight ratio between (i) and (ii) is in between 1.0:1.0 to 3.0:1.0,
(b) at least one polyamide which is different from (a),
(c) at least one impact modifier having a glass transition temperature below 0° C., and
(d) additives
wherein the impact modifier is selected from (i) ethylene-methacrylic acid copolymer, (ii) ethylene polymers and copolymers grafted with an epoxy compound, and (iii) olefin or acrylic acid or anhydride terpolymers.
2. The polyamide composition according to claim 1 , wherein the diacid comprises 9 to 40 carbon atoms.
3. The polyamide composition according to claim 1 , wherein the diacid comprises 36 carbon atoms.
4. The polyamide composition according to claim 1 , wherein the weight ratio between (i) and (ii) is in between 2.0:1.0 to 3.0:1.0.
5. The polyamide composition according to claim 1 , wherein the additives (d) are at least one selected from the group consisting of plasticizers, antioxidants, stabilizers, nucleating agents, dyes, pigments, flame retardants, lubricants, UV absorbers, antistats, fungistats, bacteriostats and IR absorbing materials.
6. A process for preparing a polyamide composition according to claim 1 , the process comprising mixing the polyamide copolymer (a), the polyamide (b), the impact modifier (c) and the additives (d).
7. A shaped article, comprising the polyamide composition according to claim 1 .
8. A method of using the polyamide composition according to claim 1 , the method comprising using the polyamide composition for a shaped article.
9. The method of using according to claim 8 , wherein the shaped article is obtained by moulding, extrusion and blow-moulding.
10. The polyamide composition according to claim 1 , wherein said at least one impact modifier has a Tg below −20° C.
11. A tubular or pipe multilayer structure, comprising an innermost layer, a middle layer and an outermost layer, wherein the innermost layer and the outermost layer, independent of one another, comprises
(a) a polyamide copolymer obtained by reacting
(i) ε-caprolactam, and
(ii) a mixture of hexamethylenediamine with a diacid comprising at least 9 carbon atoms, wherein the weight ratio between (i) and (ii) is in between 1.0:1.0 to 3.0:1.0,
wherein the middle layer comprises
(b) at least one polyamide which is different from (a), and
wherein at least one impact modifier (c) having a glass transition temperature below 0° C. and additives (d) are present in at least one of the innermost layers, the middle layer and the outermost layer.
12. The structure according to claim 11 , wherein the tubular or pipe multilayer structure has an opening at each end thereof.
13. The structure according to claim 11 , having a tensile modulus of at least 90 MPa determined according to ISO 527-1 at 23° C. and an Izod notched impact resistance at 23° C. of at least 40 KJ/m 2 determined according to ISO 180/A.
14. The structure according to claim 11 , which is capable of meeting a requirement of stress cracking resistance measured in ZnCl 2 solution in accordance with SAE J844 for 200 h duration.
15. The structure according to claim 11 , wherein the structure is selected from the group consisting of an air brake tube, air conditioning tube and a fuel pipe.