Film and method of manufacturing fluororesin composition
An object of the invention is to provide a film having excellent weatherability. The present invention provides a film comprising: a base layer formed of a thermoplastic resin, and a fluororesin layer laminated to one face of the base layer, wherein the fluororesin layer contains a tetrafluoroethylene resin and a photostabilizer. The present invention also provides a method of manufacturing a fluororesin composition suitable for manufacturing the film. The method of manufacturing comprises a dissolving step in which a photostabilizer is dissolved in ester-based, ketone-based, or aromatic solvent to obtain a solution and a mixing step in which the solution is mixed with a fluororesin comprising tetrafluoroethylene resin.
1. A film comprising:
a base layer formed of a thermoplastic resin, and
a fluororesin layer laminated to one face of the base layer,
wherein:
the fluororesin layer consists of a tetrafluoroethylene resin and a photostabilizer,
the tetrafluoroethylene resin is obtained by a curing reaction of a hydroxy group-containing tetrafluoroethylene polymer and a curing agent,
the photostabilizer is any single compound or combination of two or more compounds selected from the group consisting of: a triazine-based ultraviolet absorber, benzotriazole-based ultraviolet absorber, benzophenone-based ultraviolet absorber, and hindered amine-based photostabilizer,
the acid value of the hydroxy group-containing tetrafluoroethylene polymer is 0.5 mg KOH/g to 100 mg KOH/g,
only one fluororesin layer is laminated to the one face of the base layer, and
the thickness of the fluororesin layer is 1 μm to 20 μm.
2. The film according to claim 1 , wherein the photostabilizer is the triazine-based ultraviolet absorber.
3. The film according to claim 1 , wherein the thermoplastic resin is a polyester-based resin.
4. The film according to claim 1 , wherein the film is transparent.
5. The film according to claim 1 , further comprising an adhesive layer laminated to a face of the base layer that is opposite from the one face.
6. The film according to claim 5 , wherein the adhesive layer is formed of an acrylic resin composition.
7. The film according to claim 5 , wherein a separator is laminated to the face, among two faces of the adhesive layer, which is opposite to the face in contact with the base layer.
8. The film according to claim 1 , wherein the film is for outdoor use.
9. The film according to claim 1 , wherein the film is used for covering a face having letters or patterns formed thereon.
10. The film according to claim 9 , wherein the face is a metal face or a resin face.