IP Library Granted Patent US 12,406,997
Granted Patent B2
US 12,406,997 · App. 16/524,693 · Granted Sep 2, 2025

Anode-free solid state battery having a pseudo-solid lithium gel layer

Inventors: Ken Ogata (Kanagawa, JP); Yang Yang (Kanagawa, JP); Hajime Hoshi (Kanagawa, JP); Jungho Kim (Kanagawa, JP); Masatsugu Nakano (Kanagawa, JP); Hiroshi Imoto (Kanagawa, JP)
Assignee: TeraWatt Technology Inc.
H01M4/628H01M10/0565H01M10/0585H01M50/461H01M2300/0085
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,406,997
App. No.
16/524,693
Granted
Sep 2, 2025
Kind
B2
Abstract

An anti-dendrite anode-free solid-state battery (SSB) can include a cathode layer; an anode current collector layer; and a lithium gel separator layer between the cathode layer and the anode current collector layer. An anti-dendrite layer may also be present located between the lithium gel separator layer and the anode current collector layer. The anti-dendrite layer can help discourage dendrite formation.

Claims (44)

1. An anti-dendrite anode-free solid-state battery, comprising:

a cathode layer comprising lithium ions;

an anode current collector layer comprising copper;

a lithium-gel separator layer between the cathode layer and the anode current collector layer, wherein the lithium-gel separator layer comprises:

a first adhesive layer;

a second adhesive layer; and

a lithium gel layer located between the first adhesive layer and the second adhesive layer, wherein the lithium-gel separator layer comprises:

a non-reactive scaffold having spaces within the non-reactive scaffold; and

a lithium gel formed from a liquid electrolyte filled in the spaces and comprising a salt, a solvent, and a cross-linked polymer of a polymer additive and a cross-linker additive; and

an anti-dendrite layer located between the lithium-gel separator layer and the anode current collector layer, wherein the anti-dendrite layer comprises one or more materials selected from the group consisting of: carbon black; acetylene black; ketchen black; silver; zinc; gold; bismuth; tin; polymide (PI); polyacrylic acid (PAA); and carboxymethyl cellulose styrene-butadiene rubber (CMC-SBR); and

an interfacial bonding layer deposited directly onto the anode current collector layer such that the interfacial bonding layer is in direct contact on a first side with the anode current collector layer, wherein the interfacial bonding layer consists of a conductive agent, metal particles, and a binder material, and wherein the binder material is selected from the group consisting of polyvinylidene fluoride (PvDF), styrene butadiene rubber and sodium carboxyl methyl cellulose (SBR/CMC), poly (acrylic acid) (PAA), and any combinations thereof, the conductive agent is selected from the group consisting of acetylene black, carbon black, and a combination thereof, the metal particles are selected from the group consisting of Bi particles, Sn particles, Ag particles, Au particles, Pt particles, and any combinations thereof, the interfacial bonding layer is free from lithium and encourages formation of lithium deposits between the interfacial bonding layer and the lithium deposits,

wherein a lithium metal layer plates between the anti-dendrite layer and the interfacial bonding layer when the anode-free solid-state battery is charging.

2. The anti-dendrite anode-free solid-state battery of claim 1 , wherein the non-reactive scaffold has a spider-web structure with a porosity of between 10% and 90%.

3. The anti-dendrite anode-free solid-state battery of claim 2 , wherein the first adhesive layer and the second adhesive layer comprises a lithium-conductor ceramic.

4. The anti-dendrite anode-free solid-state battery of claim 1 , wherein the first adhesive layer contacts the non-reactive scaffold on a first side and the second adhesive layer contacts the non-reactive scaffold on a second side.

5. The anti-dendrite anode-free solid-state battery of claim 1 wherein the anti-dendrite layer is between 0.05 micrometers and 10 micrometers in thickness.

6. The anti-dendrite anode-free solid-state battery of claim 1 wherein the anti-dendrite layer consists of an alloy of one or more metals selected from the group consisting of: silver; zinc; gold; bismuth; and tin.

7. The anti-dendrite anode-free solid-state battery of claim 1 , wherein the interfacial bonding layer has a density between 0.1 and 2.0 grams per cubic centimeter.

8. The anti-dendrite anode-free solid-state battery of claim 1 , further comprising an aluminum cathode current collector.

9. A method for creating an anti-dendrite anode-free solid-state battery, the method comprising:

depositing an anti-dendrite layer onto an anode current collector layer, wherein the anode current collector layer comprises copper, the anti-dendrite layer comprises one or more materials selected from the group consisting of: carbon black; acetylene black; ketchen black; silver; zinc; gold; bismuth; tin; polymide (PI); polyacrylic acid (PAA); and carboxymethyl cellulose styrene-butadiene rubber (CMC-SBR);

creating a lithium-gel separator layer, wherein creating the lithium-gel separator layer comprises:

attaching a first adhesive layer to a non-reactive scaffold having spaces within the non-reactive scaffold;

attaching a second adhesive layer to the non-reacting scaffold; and

permeating a liquid electrolyte into the non-reactive scaffold, wherein the liquid electrolyte comprises a salt, a solvent, a polymer additive, and a cross-linker additive, the liquid electrolyte is filled in the spaces;

layering a cathode current collector layer onto a cathode layer, the cathode layer comprising lithium ions;

layering an interfacial bonding layer directly onto the anode current collector layer such that the interfacial bonding layer is in direct contact on a first side with the anode current collector layer and in direct contact on a second side with the anti-dendrite layer, wherein the interfacial bonding layer consists of a conductive agent, metal particles, and a binder material, and wherein the binder material is selected from the group consisting of polyvinylidene fluoride (PvDF), styrene butadiene rubber and sodium carboxyl methyl cellulose (SBR/CMC), poly (acrylic acid) (PAA), and any combinations thereof, the conductive agent is selected from the group consisting of acetylene black, carbon black, and a combination thereof, the metal particles are selected from the group consisting of Bi particles, Sn particles, Ag particles, Au particles, Pt particles, and any combinations thereof, the interfacial bonding layer is free from lithium and encourages formation of lithium deposits between the interfacial bonding layer and the anti-dendrite layer;

layering the lithium-gel separator layer between the anti-dendrite layer and the cathode layer, thereby creating a layered battery stack of: the cathode current collector layer, the cathode layer, the lithium-gel separator layer, the anti-dendrite layer, the interfacial bonding layer, and the anode current collector layer;

packaging the layered battery stack in a flexible pouch cell; and

applying heat and pressure to the layered battery stack within the flexible pouch cell to convert the liquid electrolyte into a lithium gel comprising a cross-linked polymer of the polymer additive and the cross-linker additive,

wherein a lithium metal layer plates between the anti-dendrite layer and the interfacial bonding layer when the anode-free solid-state battery is charging.

10. The method for creating the anti-dendrite anode-free solid-state battery of claim 9 , wherein the non-reactive scaffold has a spider-web structure with a porosity of between 10% and 90%.

11. The method for creating the anti-dendrite anode-free solid-state battery of claim 9 wherein the polymer additive comprises Poly(4-vinylpyridine)(P4VP); and the cross-linker additive is selected from the group consisting of N,N,N′,N′-Tetra(trifluoromethanesulfonyl)-dodecane-1,12-diamine (C12TFSA), N,N,N′,N′-Tetra(trifluoromethanesulfonyl)-hexane-1,6-diamine (C6TFSA), and a combination thereof.

12. The method for creating the anti-dendrite anode-free solid-state battery of claim 11 , wherein applying the heat causes the liquid electrolyte to become the lithium gel.

13. The method for creating the anti-dendrite anode-free solid-state battery of claim 9 , wherein the method further comprises inserting a temperature probe to monitor temperature of the anti-dendrite anode-free solid-state battery.

14. The method for creating the anti-dendrite anode-free solid-state battery of claim 13 , wherein the anti-dendrite layer is between 0.05 micrometers and 10 micrometers in thickness.

15. The method for creating the anti-dendrite anode-free solid-state battery of claim 9 , further comprising:

compressing the flexible pouch cell in a jig press; and

charging and discharging the layered battery stack within the jig press.

16. The method for creating the anti-dendrite anode-free solid-state battery of claim 9 , wherein the anti-dendrite layer consists of an alloy of one or more metals selected from the group consisting of: silver; zinc; gold; bismuth; and tin.

17. The anti-dendrite anode-free solid-state battery of claim 1 , wherein the conductive agent is in a form of carbon particles with an average size from 3 nm to 20 nm.

18. The anti-dendrite anode-free solid-state battery of claim 1 , wherein the binder material is selected from the group consisting of styrene butadiene rubber and sodium carboxyl methyl cellulose (SBR/CMC), poly (acrylic acid) (PAA), and a combination thereof.

19. The anti-dendrite anode-free solid-state battery of claim 1 , wherein the polymer additive comprises Poly(4-vinylpyridine)(P4VP); and the cross-linker additive is selected from the group consisting of N,N,N′,N′-Tetra(trifluoromethanesulfonyl)-dodecane-1,12-diamine (C12TFSA), N,N,N′,N′-Tetra(trifluoromethanesulfonyl)-hexane-1,6-diamine (C6TFSA), and a combination thereof.

20. The anti-dendrite anode-free solid-state battery of claim 1 , wherein the binder material is styrene butadiene rubber and sodium carboxyl methyl cellulose (SBR/CMC).

Assignments (4)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Sep 15, 2020
From: OGATA, KEN; YANG, YANG; HOSHI, HAJIME; KIM, JUNGHO; NAKANO, MASATSUGU; IMOTO, HIROSHI
To: CHONGQING JINKANG NEW ENERGY AUTOMOBILE CO., LTD; SF MOTORS INC.
Reel/Frame 053775/0522 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jun 3, 2020
From: CHONGQING JINKANG NEW ENERGY AUTOMOBILE CO., LTD.
To: SF MOTORS, INC.
Reel/Frame 052823/0463 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jun 3, 2020
From: SF MOTORS, INC.
To: TERAWATT TECHNOLOGY INC.
Reel/Frame 052827/0684 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Oct 22, 2019
From: OGATA, KEN; YANG, YANG; HOSHI, HAJIME; KIM, JUNGHO; NAKANO, MASATSUGU; IMOTO, HIROSHI
To: CHONGQING JINKANG NEW ENERGY AUTOMOBILE CO., LTD.; SF MOTORS INC.
Reel/Frame 050796/0239 →
Continuity (1)
Related Publication 20210036328A1 · Feb 4, 2021
References Cited (76)
US 5538814A · Kamauchi et al. · 1996 [cited by applicant]
US 9564656B1 · Zhamu · 2017 [cited by examiner]
US 11271253B2 · Ogata et al. · 2022 [cited by applicant]
US 12125975B2 · Ogata et al. · 2024 [cited by applicant]
US 20010041294A1 · Chu · 2001 [cited by examiner]
US 20060019168A1 · Li · 2006 [cited by examiner]
US 20060063072A1 · Li · 2006 [cited by examiner]
US 20080241685A1 · Hinoki · 2008 [cited by examiner]
US 20110287325A1 · Zaghib et al. · 2011 [cited by applicant]
US 20120135308A1 · Loveridge · 2012 [cited by examiner]
US 20130017441A1 · Affinito · 2013 [cited by examiner]
US 20130095377A1 · Yamin · 2013 [cited by examiner]
US 20140255796A1 · Matsuoka · 2014 [cited by examiner]
US 20140329130A1 · Kanamura · 2014 [cited by examiner]
US 20150236322A1 · Laramie et al. · 2015 [cited by applicant]
US 20150243997A1 · Park · 2015 [cited by examiner]
US 20150325838A1 · Tamaki · 2015 [cited by examiner]
US 20150349338A1 · Zhao · 2015 [cited by examiner]
US 20160087305A1 · Yoneda et al. · 2016 [cited by applicant]
US 20160329567A1 · Lee et al. · 2016 [cited by applicant]
US 20160344010A1 · Zhamu et al. · 2016 [cited by applicant]
US 20170011486A1 · Agrawal et al. · 2017 [cited by applicant]
US 20170077486A1 · Ishii · 2017 [cited by examiner]
US 20170179520A1 · Seo · 2017 [cited by examiner]
US 20170214090A1 · Maeda · 2017 [cited by applicant]
US 20170301951A1 · Carignan et al. · 2017 [cited by applicant]
US 20170301957A1 · Park et al. · 2017 [cited by applicant]
US 20170338465A1 · Holme et al. · 2017 [cited by applicant]
US 20180102535A1 · Xie · 2018 [cited by examiner]
US 20180309093A1 · Amatucci et al. · 2018 [cited by applicant]
US 20190058210A1 · Dai · 2019 [cited by examiner]
US 20190109311A1 · Shin · 2019 [cited by examiner]
US 20190214685A1 · Chang et al. · 2019 [cited by applicant]
US 20200052350A1 · Zhamu · 2020 [cited by examiner]
US 20200083525A1 · Lee · 2020 [cited by examiner]
US 20200203757A1 · Park · 2020 [cited by examiner]
US 20200220142A1 · Imoto et al. · 2020 [cited by applicant]
CN 101036251A · 2007 [cited by applicant]
CN 103703587B · 2016 [cited by applicant]
CN 109065814A · 2018 [cited by applicant]
EP 3605678A1 · 2020 [cited by applicant]
JP 11283673A · 1999 [cited by applicant]
JP 2003203677A · 2003 [cited by applicant]
JP 2005142156A · 2005 [cited by applicant]
JP 2016091634A · 2016 [cited by applicant]
KR 20020057570A · 2002 [cited by applicant]
KR 20140082043A · 2014 [cited by applicant]
KR 20190001556A · 2019 [cited by applicant]
KR 20190079534A · 2019 [cited by applicant]
WO 2006052082A1 · 2006 [cited by applicant]
WO WO2012074089A1 · 2012 [cited by examiner]
WO 2019004699A1 · 2019 [cited by applicant]
WO 2019132449A1 · 2019 [cited by applicant]
WO 2012/074089 translation (Year: 2012). [cited by examiner]
International Search Report and Written Opinion mailed Oct. 28, 2020 in related application No. PCT/US2020/043409, all pgs. [cited by applicant]
International Search Report and Written Opinion mailed Oct. 30, 2020 in related application No. PCT/US2020/043809, all pgs. [cited by applicant]
International Search Report and Written Opinion mailed Nov. 4, 2020 in related application No. PCT/US2020/043406 all pgs. [cited by applicant]
International Search Report and Written Opinion mailed Nov. 11, 2020 in related application No. PCT/US2020/043811, all pgs. [cited by applicant]
Zhang Sheng, et. al.: “A Tin-Plated Copper Substrate for Efficient Cycling of Lithium Metal in an Aanode-Free Rechargeable Lithium Battery”, Electrochimica Acta, Elsevier, Amsterdam, NL, vol. 258, Nov. 26, 2017 (Nov. 26… [cited by applicant]
U.S. Appl. No. 16/524,690, filed Jul. 29, 2019, Final Office Action mailed Dec. 12, 2023, all pages. [cited by applicant]
U.S. Appl. No. 16/524,684, filed Jul. 29, 2019, Advisory Action Before the Filing of an Appeal Brief mailed Dec. 12, 2023. [cited by applicant]
“JP 2003203677 A Translation”, Jul. 18, 2003, 8 pages. [cited by applicant]
U.S. Appl. No. 16/524,684 , Advisory Action, Mailed on Jan. 4, 2023, 4 pages. [cited by applicant]
U.S. Appl. No. 16/524,684 , Final Office Action, Mailed on Sep. 19, 2022, 17 pages. [cited by applicant]
U.S. Appl. No. 16/524,684 , Final Office Action, Mailed on Aug. 30, 2023, 25 pages. [cited by applicant]
U.S. Appl. No. 16/524,684 , Non-Final Office Action, Mailed on Mar. 18, 2022, 19 pages. [cited by applicant]
U.S. Appl. No. 16/524,684 , Non-Final Office Action, Mailed on Feb. 8, 2023, 21 pages. [cited by applicant]
U.S. Appl. No. 16/524,684 , Notice of Allowance, Mailed on Mar. 4, 2024, 13 pages. [cited by applicant]
U.S. Appl. No. 16/524,690 , Advisory Action, Mailed on Jan. 25, 2023, 8 pages. [cited by applicant]
U.S. Appl. No. 16/524,690 , Final Office Action, Mailed on Dec. 2, 2022, 16 pages. [cited by applicant]
U.S. Appl. No. 16/524,690 , Non-Final Office Action, Mailed on Mar. 7, 2024, 26 pages. [cited by applicant]
U.S. Appl. No. 16/524,690 , Non-Final Office Action, Mailed on Jun. 14, 2022, 27 pages. [cited by applicant]
U.S. Appl. No. 16/524,700 , Non-Final Office Action, Mailed on Apr. 30, 2021, 11 pages. [cited by applicant]
U.S. Appl. No. 16/524,684, filed Jul. 29, 2019, Notice of Allowance mailed Jun. 21, 2024, all pages. [cited by applicant]
U.S. Appl. No. 16/524,690 , Final Office Action, Mailed on Sep. 19, 2024, 25 pages. [cited by applicant]
Application No. EP20754526.0 , Office Action, Mailed on Sep. 10, 2024, 9 pages. [cited by applicant]