Contacts of solar cells and other optoelectronic devices

Inventors: Yong-Hang Zhang (Scottsdale, AZ); Xin Qi (Tempe, AZ); Zheng Ju (Tempe, AZ); Jia Ding (Tempe, AZ); Tyler McCarthy (Scottsdale, AZ); Stephen Schaefer (Scottsdale, AZ)
Assignee: ARIZONA BOARD OF REGENTS ON BEHALF OF ARIZONA STATE UNIVERSITY
H10F77/211H10F71/00
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,408,474
App. No.
18/151,341
Granted
Sep 2, 2025
Kind
B2
Abstract

Contacts for solar cells and other optoelectronic devices are provided. Embodiments described herein take advantage of the surface Fermi level pinning effect to build an electrical field inside of a semiconductor to extract or inject carriers for solar cells, photodetectors, and light-emitting device applications. For example, n-type or p-type two-dimensional (2D) materials can be used in contact with an n-type semiconductor to form a “p-region” so that a p-n junction, or an i-n or n-n+ junction can be constructed. Similarly, n-type or p-type 2D materials can be used in contact with a p-type semiconductor to form an “n-region” so that an n-p junction, or an i-p or p-p+ junction can be constructed. These structures can provide sufficiently high electrical field inside the semiconductor to extract photogenerated carriers in solar cells and photodetectors or inject minority carriers for light-emitting devices.

Claims (40)

1. An optoelectronic junction, comprising:

a thin-film doped semiconductor; and

a p-contact layer comprising a two-dimensional (2D) material deposited at an interface of the thin-film doped semiconductor forming the optoelectronic junction, a thickness of the two-dimensional (2D) material being chosen to tailor a Fermi level of the two-dimensional (2D) material to overlap or fall below a valence band edge of the thin-film doped semiconductor at the interface,

wherein the thin-film doped semiconductor comprises a p-type semiconductor,

wherein the p-contact layer comprising the two-dimensional (2D) material comprises a single-layer p-type material or a double-layer p-type material, and

wherein the optoelectronic junction is a p-p+ junction.

2. The optoelectronic junction of claim 1 , wherein the two-dimensional (2D) material induces a sufficiently high electrical field inside the thin-film doped semiconductor to extract photogenerated carriers from the optoelectronic junction or inject minority carriers into the optoelectronic junction.

3. The optoelectronic junction of claim 1 , further comprises indium tin oxide disposed over the p-contact layer forming an ohmic contact.

4. The optoelectronic junction of claim 1 , wherein the p-contact layer comprises a doped Cu/Au.

5. The optoelectronic junction of claim 1 , wherein the two-dimensional (2D) material comprises one of ZnTe:As, ZnTe:Cu, or CuZnS.

6. The optoelectronic junction of claim 5 , wherein the p-contact layer comprises:

a pre-selected work-function and a pre-selected interface recombination.

7. The optoelectronic junction of claim 1 , wherein the p-contact layer comprises:

a single layer or double-layer stack of transition-metal oxide (TMO) and dichalcogenides (TMD) [(Mo, W)(O, S, Se, Te)], and GaSe two-dimensional (2D) materials configured to tailor a work-function of the p-contact layer to realize ohmic hole-selective contact with CdTe.

8. A method for forming a thin-film optoelectronic device, the method comprising:

providing a thin-film doped semiconductor; and

creating a p-contact layer by depositing a two-dimensional (2D) material at an interface of the thin-film doped semiconductor to form an optoelectronic junction,

wherein a thickness of the two-dimensional (2D) material being chosen to tailor a Fermi level of the two-dimensional (2D) material to overlap or fall below a valence band edge of the thin-film doped semiconductor at the interface,

wherein the thin-film doped semiconductor comprises a p-type semiconductor,

wherein the p-contact layer comprising the two-dimensional (2D) material comprises a single-layer p-type material or a double-layer p-type material, and

wherein the optoelectronic diode junction is a p-p+ junction.

9. The method of claim 8 , further comprising:

depositing indium tin oxide over the p-contact layer forming an ohmic contact.

10. The method of claim 8 , wherein the two-dimensional (2D) material induces a sufficiently high electrical field inside the thin-film doped semiconductor to extract photogenerated carriers from the optoelectronic diode junction or inject minority carriers into the optoelectronic diode junction.

11. The method of claim 10 , wherein the two-dimensional (2D) material comprises one of:

ZnTe:As, ZnTe:Cu, or CuZnS).

12. The method of claim 8 , wherein the p-contact layer comprises a doped Cu/Au.

13. The method of claim 12 , wherein the p-contact layer comprises:

a pre-selected work-function and a pre-selected interface recombination.

14. A contact for a solar cell comprising a thin-film doped semiconductor, the contact comprising:

a p-contact layer including a two-dimensional (2D) material deposited at an interface of the thin-film doped semiconductor forming an optoelectronic junction, a thickness of the two-dimensional (2D) material being chosen to tailor a Fermi level of the two-dimensional (2D) material to overlap or fall below a valence band edge of the thin-film doped semiconductor at the interface; and

indium tin oxide disposed over the p-contact layer forming an ohmic contact,

wherein the thin-film doped semiconductor comprises a p-type semiconductor,

wherein the p-contact layer comprising the two-dimensional (2D) material comprises a single-layer p-type material or a double-layer p-type material, and

wherein an optoelectronic junction including the thin-film doped semiconductor and the p-contact layer is a p-p+ junction.

15. The contact of claim 14 , wherein the two-dimensional (2D) material induces a sufficiently high electrical field inside the thin-film doped semiconductor to extract photogenerated carriers from the optoelectronic junction or inject minority carriers into the optoelectronic junction.

16. The contact of claim 14 , wherein the p-contact layer comprises a doped Cu/Au.

17. The contact of claim 14 , wherein the two-dimensional (2D) material comprises one of ZnTe:As, ZnTe:Cu, or CuZnS.

18. The contact of claim 14 , wherein the p-contact layer comprises a pre-selected work-function and a pre-selected interface recombination.

19. The contact of claim 14 , wherein the p-contact layer comprises a single layer or double-layer stack of transition-metal oxide (TMO) and dichalcogenides (TMD) [(Mo, W) (O, S, Se, Te)], and GaSe two-dimensional (2D) materials configured to tailor a work-function to realize ohmic hole-selective contact with CdTe.

Assignments (1)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jun 5, 2023
From: ZHANG, YONG-HANG; QI, XIN; JU, ZHENG; DING, JIA; MCCARTHY, TYLER; SCHAEFER, STEPHEN
To: ARIZONA BOARD OF REGENTS ON BEHALF OF ARIZONA STATE UNIVERSITY
Reel/Frame 063854/0075 →
Continuity (2)
Provisional Application 63297111 · Jan 6, 2022
Related Publication 20230215961A1 · Jul 6, 2023
References Cited (20)
US 11063164B1 · Engel · 2021 [cited by examiner]
US 20150255661A1 · Liang · 2015 [cited by examiner]
US 20200157125A1 · Irwin · 2020 [cited by examiner]
WO WO2017172962A1 · 2017 [cited by examiner]
Yu Zhang, Ping Su, Linqing Liu, Pengfei Qiu, Li Su, Guangsheng Fu, Wei Yu, The effect of MoS2 modulated doping with molybdenum-oxide on the photovoltaic performance for MoS2/n-Si heterojunction solar cells, Solar Energy… [cited by examiner]
Zhao et al. Monocrystalline CdTe solar cells with open-circuit voltage over 1 V and efficiency of 17%, Nat. Energy 1, 16067, 2016, 22 pages. [cited by applicant]
Becker et al., Loss Analysis of Monocrystalline CdTe Solar Cells With 20% Active-Area Efficiency, IEEE J. Photovoltaics, 99, 2017, pp. 1-6. [cited by applicant]
Becker et al., Monocrystalline CdTe/MgCdTe double-heterostructure solar cells with ZnTe hole contacts, IEEE J. Photovoltaics, 7, 2016, pp. 307-312. [cited by applicant]
Sun et al., Band alignment of two-dimensional metal monochalcogenides MXs (M=Ga,In;X=S,Se,Te), AIP Advances, 7, 095120, 2017, 6 pages. [cited by applicant]
Woods-Robinson et al., Wide Band Gap Chalcogenide Semiconductors, Chem. Rev., 120, 2020, pp. 4007-4055. [cited by applicant]
Dreon et al. 23.5%-efficient silicon heterojunction silicon solar cell using molybdenum oxide as hole-selective contact, Nano Energy, 70, 104495, 2020, 8 pages. [cited by applicant]
Zhou et al., Large Area Growth and Electrical Properties of p-Type WSe2 Atomic Layers, Nano Lett. 2015, 15, 1, pp. 709-713. [cited by applicant]
Battaglia et al., Hole Selective MoOx Contact for Silicon Solar Cells, Nano Lett . 14, 2014, pp. 967-971. [cited by applicant]
Swanson et al. CdCI2 passivation of polycrystalline CdMgTe and CdZnTe absorbers for tandem photovoltaic cells, J. Appl. Phys. 123, 203101, 2018, 11 pages. [cited by applicant]
Becker et al., Monocrystalline 1.7-eV-bandgap MgCdTe solar cell with 11.2% efficiency, IEEE Journal of Photovoltaics, vol. 8, No. 2, Mar. 2018, pp. 581-586. [cited by applicant]
Becker et al., CuZnS hole contacts on monocrystalline CdTe solar cells, IEEE Photovoltaic Specialist Conference, 2017, pp. 3410-3412. [cited by applicant]
Chen et al., The unique photocatalysis properties of a 2D vertical MoO2/WO2 heterostructure: a first principles study, Journal of Physics D: Applied Physics, 51, 265106, 2018, 7 pages. [cited by applicant]
Kang et al., Band offsets and heterostructures of two-dimensional semiconductors, Applied Physics Letters, 102, 012111, 2013, 5 pages. [cited by applicant]
Metzger et al., Exceeding 20% efficiency with in situ group V doping in polycrystalline CdTe solar cells, Nature Energy, vol. 4, Oct. 2019, pp. 837-845. [cited by applicant]
Burst et al., CdTe solar cells with open-circuit voltage breaking the 1 V barrier, Nat. Energy 1, 16015, 2016, 8 pages. [cited by applicant]