Coating compositions containing low molecular weight chitosan composition
Paint and coating compositions including a low molecular weight chitosan that may be incorporated in a coating composition at higher loading levels, which exhibits one or more of improved elongation, improved thermocycling characteristics, reduced leaching of coating components, are lesser susceptibility to fungal and mildew defacement than conventional coatings or coatings containing higher molecular weight chitosan compounds, articles coated in the same, and methods for making said coatings and coated articles.
1. A method of making a coating composition comprising:
blending a binder, a surfactant, and a first aqueous carrier to form a pre-thin:
adding an aqueous solution of chitosan having a number average molecular weight of at most 40,000 or a weight average molecular weight of at most 75,000 or a z-average molecular weight of at most 200,000 and having a pH of less than 6.5, a pigment and a second aqueous carrier liquid, optional additives, and a base to precipitate the chitosan into precipitated chitosan;
grinding, in grind stage, the pigment with the second aqueous carrier liquid, precipitated chitosan and optional additives, to disperse the pigment, precipitated chitosan, and optional additives into a grind paste;
adding, in a wash stage using a wash liquid, the grind paste to the pre-thin;
blending, in a thindown stage, the grind paste and the pre-thin to form a coating composition having a pH of about 8 to about 10.
2. The method of claim 1 , further comprising dispensing the coating composition into a storage container.
3. The method of claim 2 , wherein the storage container is a paint can.
4. The method of claim 1 , wherein the aqueous solution of chitosan is chitosan in aqueous acetic acid.
5. The method of claim 1 , wherein the chitosan is present in the aqueous solution of chitosan at a concentration of at least 3.0% and at most 4.0% by mass of the total components of the solution.
6. The method of claim 1 , wherein the coating composition comprises 13% to 30% by weight pigment and the pigment is titanium dioxide.
7. The method of claim 1 , wherein the coating composition has a pigment volume concentration below 60.
8. The method of claim 1 , wherein the coating composition is about 30% to about 60% by weight solids.
9. The method of claim 1 , wherein the chitosan has a particle size of less than 30 microns in the coating composition.
10. The method of claim 1 , wherein the chitosan has a particle size of less than 20 microns in the coating composition.
11. The method of claim 1 , wherein the chitosan has a particle size of less than 16 microns in the coating composition.
12. The method of claim 1 , wherein the chitosan is present in the coating composition at a concentration of 0.02 to 1.0 weight percent based on weight of dry coating solids.
13. The method of claim 1 , wherein the binder includes an acrylic latex.
14. The method of claim 1 , wherein the binder includes a polyurethane dispersion.
15. The method of claim 1 , wherein the binder includes a styrene acrylic latex.
16. The method of claim 1 , wherein the binder includes a vinyl acrylic latex.