Polycrystalline diamond-on-metal bearings for use in cryogenic conditions
Bearing assemblies for use in low-temperature conditions are provided. The bearing assemblies include polycrystalline diamond bearing elements having diamond bearing surfaces and opposing bearing elements having metal bearing surfaces. The metal bearing surfaces include a metal that contains at least 2 weight percent of a diamond solvent-catalyst based on a total weight of the metal. The metal is ductile at temperatures ranging from −150° C. to −253° C. The metal bearing surface is in sliding contact with the diamond bearing surface.
1 . A bearing assembly for use in low-temperature conditions, the bearing assembly comprising: a cryogenically treated polycrystalline diamond bearing element having a diamond bearing surface; an opposing bearing element having a metal bearing surface, wherein the metal bearing surface comprises a metal, the metal containing at least 2 weight percent of a diamond solvent-catalyst based on a total weight of the metal, and wherein the metal is ductile at a temperature of −150° C.; and wherein the metal bearing surface is in contact with the diamond bearing surface.
2 . The bearing assembly of claim 1 , wherein the metal is ductile at temperatures ranging from −150° C. to −253° C.
3 . The bearing assembly of claim 1 , wherein the metal is ductile at temperatures ranging from −150° C. to −196° C. when subjected to a Charpy impact test performed in accordance with ASTM-E23-18.
4 . The bearing assembly of claim 1 , wherein the metal bearing surface is in sliding contact with the diamond bearing surface.
5 . The bearing assembly of claim 1 , wherein the metal is a metal alloy.
6 . The bearing assembly of claim 5 , wherein the metal is an alloy steel.
7 . The bearing assembly of claim 6 , wherein the alloy steel contains from 3.5 to 11 wt. % nickel based on a total weight of the alloy steel.
8 . The bearing assembly of claim 5 , wherein the metal is a nickel alloy.
9 . The bearing assembly of claim 5 , wherein the metal is a titanium alloy.
10 . The bearing assembly of claim 5 , wherein the metal is an austenitic steel.
11 . The bearing assembly of claim 1 , wherein the metal is a metal alloy, and wherein the diamond solvent-catalyst comprises iron, cobalt, nickel, titanium, copper, chromium, manganese, tantalum, or a combination thereof.
12 . The bearing assembly of claim 11 , wherein the metal contains at least 2 weight percent of iron based on the total weight of the metal.
13 . The bearing assembly of claim 11 , wherein the metal contains at least 2 weight percent of cobalt based on the total weight of the metal.
14 . The bearing assembly of claim 11 , wherein the metal contains at least 2 weight percent of nickel based on the total weight of the metal.
15 . The bearing assembly of claim 11 , wherein the metal contains at least 2 weight percent of titanium based on the total weight of the metal.
16 . The bearing assembly of claim 11 , wherein the metal contains at least 2 weight percent of copper based on the total weight of the metal.
17 . The bearing assembly of claim 11 , wherein the metal contains at least 2 weight percent of chromium based on the total weight of the metal.
18 . The bearing assembly of claim 11 , wherein the metal contains at least 2 weight percent of manganese based on the total weight of the metal.
19 . The bearing assembly of claim 11 , wherein the metal is a metal alloy that contains at least 2 weight percent of tantalum based on the total weight of the metal.
20 . The bearing assembly of claim 1 , wherein the metal is softer than a superhard material.
21 . The bearing assembly of claim 1 , wherein the metal has a hardness value of less than 25 GPa as determined in accordance with ASTM E92-17.
22 . The bearing assembly of claim 1 , wherein the opposing bearing element is a metal cylinder shaft.
23 . The bearing assembly of claim 1 , wherein the bearing assembly comprises a bearing ring having a plurality of the cryogenically treated polycrystalline diamond bearing elements with diamond bearing surfaces thereon, and wherein the opposing bearing element is a metal cylinder shaft positioned within the bearing ring.
24 . The bearing assembly of claim 1 , wherein the cryogenically treated polycrystalline diamond bearing element is a cryogenically treated polycrystalline diamond compact.
25 . The bearing assembly of claim 1 , wherein a coefficient of friction between the diamond bearing surface and the metal bearing surface is 0.09 or less.
26 . The bearing assembly of claim 1 , wherein the bearing assembly is a radial bearing, an axial bearing, a cam and cam follower assembly, or a roller ball assembly.
27 . The bearing assembly of claim 1 , wherein the bearing assembly is a conical bearing or a linear bearing.
28 . The bearing assembly of claim 1 , wherein the bearing assembly is a journal bearing.
29 . The bearing assembly of claim 1 , wherein the diamond bearing surface and the metal bearing surface are power transmission surfaces.
30 . The bearing assembly of claim 1 , wherein the metal is ductile at temperatures in which hydrogen, methane, natural gas, oxygen, nitrogen, and helium are in a liquid state.
31 . The bearing assembly of claim 1 , wherein the metal is softer than tungsten carbide (WC).
32 . The bearing assembly of claim 1 , wherein the metal has a hardness value of less than 15 GPa as determined in accordance with ASTM E92-17.
33 . The bearing assembly of claim 1 , wherein a surface roughness of the diamond bearing surface is 20 μin Ra or less.
34 . The bearing assembly of claim 1 , wherein the bearing assembly comprises a plurality of the cryogenically treated polycrystalline diamond bearing elements having diamond bearing surfaces, and wherein the metal bearing surface is in sliding contact with each of the diamond bearing surfaces.
35 . The bearing assembly of claim 1 , wherein the cryogenically treated polycrystalline diamond bearing element is leached and backfilled.
36 . The bearing assembly of claim 1 , wherein the cryogenically treated polycrystalline diamond bearing element comprises a thermally stable polycrystalline diamond sintered with a ceramic binder.
37 . The bearing assembly of claim 1 , wherein the opposing bearing element is cryogenically treated.
38 . A system for use in low-temperature conditions, the system comprising: a bearing assembly including a cryogenically treated polycrystalline diamond bearing element and an opposing bearing element; the polycrystalline diamond bearing element having a diamond bearing surface; the opposing bearing element having a metal bearing surface, wherein the metal bearing surface comprises a metal, the metal containing at least 2 weight percent of a diamond solvent-catalyst based on a total weight of the metal, and wherein the metal is ductile at a temperature of −150° C.; and wherein the metal bearing surface is in contact with the diamond bearing surface.
39 . The system of claim 38 , wherein the system is operated in an extra-atmospheric environment.
40 . The system of claim 38 , wherein the system is the turbine engine that operates on cryogenic fuel.
41 . The system of claim 40 , wherein the system is operated in an extra-atmospheric environment.
42 . A bearing assembly for use in low-temperature conditions, the bearing assembly comprising: a cryogenically treated polycrystalline diamond bearing element having a diamond bearing surface; a cryogenically treated opposing bearing element having a metal bearing surface, wherein the metal bearing surface comprises a metal alloy, the metal alloy containing at least 2 weight percent of a diamond solvent-catalyst based on a total weight of the metal alloy, wherein the metal alloy is ductile at a temperature of −150° C. when subjected to a Charpy impact test performed in accordance with ASTM-E23-18, and wherein the metal alloy has a hardness value of less than 25 GPa as determined in accordance with ASTM E92-17; and wherein the metal bearing surface is in sliding contact with the diamond bearing surface.
43 . A system for use in low-temperature conditions, the system comprising:
a bearing assembly including a cryogenically treated polycrystalline diamond bearing element and an opposing bearing element; the cryogenically treated polycrystalline diamond bearing element having a diamond bearing surface; the opposing bearing element having a metal bearing surface, wherein the metal bearing surface comprises a metal, the metal containing at least 2 weight percent of a diamond solvent-catalyst based on a total weight of the metal, wherein the metal is ductile at a temperature of −150° C. to −196° C. when subjected to a Charpy impact test performed in accordance with ASTM-E23-18, and wherein the metal has a hardness value of less than 25 GPa as determined in accordance with ASTM E92-17; wherein the metal bearing surface is in sliding contact with the diamond bearing surface.
44 . A bearing assembly for use in low-temperature conditions, the bearing assembly comprising: a cryogenically treated polycrystalline diamond bearing element having a diamond bearing surface; an opposing bearing element having a metal bearing surface, wherein the metal bearing surface comprises a metal, the metal containing at least 2 weight percent of a diamond solvent-catalyst based on a total weight of the metal; and wherein the metal bearing surface is in contact with the diamond bearing surface.
45 . The bearing assembly of claim 44 , wherein the metal is a metal alloy.
46 . The bearing assembly of claim 45 , wherein the metal alloy is an alloy steel.
47 . The bearing assembly of claim 46 , wherein the alloy steel contains from 3.5 to 11 wt. % nickel based on a total weight of the alloy steel.
48 . The bearing assembly of claim 45 , wherein the metal alloy is a nickel alloy.
49 . The bearing assembly of claim 45 , wherein the metal alloy is a titanium alloy.
50 . The bearing assembly of claim 45 , wherein the metal alloy is an austenitic steel.