Dielectric material, device including the same, and method of preparing the dielectric material

Inventors: Sung-Yoon Chung (Daejeon, KR); Ji-Sang An (Daejeon, KR)
Assignee: KOREA ADVANCED INSTITUTE OF SCIENCE AND TECHNOLOGY
H01G4/1227C04B35/4682C04B35/64H01G4/30C04B2235/3236C04B2235/3286C04B2235/3418C04B2235/656C04B2235/768C04B2235/781C04B2235/785C04B2235/85
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,512,265
App. No.
18/339,597
Granted
Dec 30, 2025
Kind
B2
Abstract

Provided are a dielectric material, a device including the same, and a method of preparing the dielectric material. The dielectric material includes a polycrystalline oxide including a plurality of crystal grain bulks and grain boundaries located between the plurality of crystal grain bulks, and the polycrystalline oxide includes an indium dopant in the grain boundaries.

Claims (40)

1 . A dielectric material comprising

a polycrystalline oxide including a plurality of crystal grain bulks and grain boundaries located between the plurality of crystal grain bulks,

wherein the polycrystalline oxide comprises an indium dopant in the grain boundaries, and

charge compensation of the indium (In) dopant occurs in the grain boundaries via barium (Ba) vacancies rather than oxygen (O) vacancies.

2 . The dielectric material according to claim 1 , wherein the polycrystalline oxide comprises an oxide represented by Formula 1 below:

ABO 3   Formula 1

wherein in Formula 1,

A comprises Ba and further comprises at least one element selected from elements of Group 2 of the periodic table, and

B comprises Ti and further comprises at least one element selected from transition metal elements.

3 . The dielectric material according to claim 1 , wherein the polycrystalline oxide comprises BaTiO 3 , (Ba 1-x Ca x )TiO 3 , (Ba 1-x Sr x )TiO 3 , Ba(Ti 1-y Zr y )O 3 , Ba(Ti 1-y Hf y )O 3 , Ba(Ti 1-y Sn y )O 3 , Ba(Ti 1-y Ce y )O 3 , (Ba 1-x Ca x )(Ti 1-y Zr y )O 3 , (Ba 1-x Sr x )(Ti 1-y Hf y )O 3 , (Ba 1-x Sr x )(Ti 1-y Sn y )O 3 , (Ba 1-x Ca x )(Ti 1-y Ce y )O 3 , (Ba 1-x Sr x )(Ti 1-y Ce y )O 3 , or any combination thereof, wherein 0<x<1 and 0<y<1.

4 . The dielectric material according to claim 1 , wherein the indium dopant occupies interstices in the grain boundaries.

5 . The dielectric material according to claim 1 , wherein the indium dopant occupies square-planar interstices in the grain boundaries.

6 . The dielectric material according to claim 1 , wherein the crystal grain bulks have a grain size of about 50 nm to about 300 nm.

7 . The dielectric material according to claim 1 , wherein a content of the indium dopant is from about 0.5 mol % to about 10 mol % based on 100 mol % of a total Ti content of the polycrystalline oxide.

8 . The dielectric material according to claim 1 , wherein a width of a portion of the indium dopant segregated into the grain boundaries is 10 nm or less.

9 . The dielectric material according to claim 1 , wherein the dielectric material has a dielectric loss of 1% or less in a frequency range of 100 Hz to 10 MHz.

10 . The dielectric material according to claim 1 , wherein the dielectric material has a variation of less than 10% in relative permittivity under conditions of applying a DC electric field of 0 V/μm to 5 V/μm.

11 . The dielectric material according to claim 1 , wherein the dielectric material has a variation of −15% to +15% in permittivity at 150° C.

12 . The dielectric material according to claim 1 , wherein the dielectric material has a variation of −22% to +22% in permittivity at 200° C.

13 . A device comprising:

a first electrode;

a second electrode opposite to the first electrode; and

a dielectric layer located between the first electrode and the second electrode and having a single-layered structure or a multi-layered structure including two or more layers,

wherein the dielectric layer comprises the dielectric material according to claim 1 .

14 . The device according to claim 13 , wherein the device is a capacitor.

15 . The device according to claim 13 , wherein the device comprises:

a plurality of first electrodes;

a plurality of second electrodes,

the plurality of first electrodes and the plurality of second electrodes being alternately arranged; and

dielectric layers respectively interposed between each of the plurality of first electrodes and each of the plurality of second electrodes.

16 . A method of preparing the dielectric material according to claim 1 , the method comprising:

preparing a polycrystalline oxide powder;

mixing the polycrystalline oxide powder with an indium dopant precursor to prepare a mixture; and

performing first heat treatment on the mixture in a reducing atmosphere at a temperature of 1300° C. or below to obtain a sintered product.

17 . The method according to claim 16 , wherein the polycrystalline oxide comprises an oxide represented by Formula 1 below:

ABO 3   Formula 1

wherein in Formula 1,

A comprises Ba and further comprises at least one element selected from divalent cations, and

B comprises Ti and further comprises at least one element selected from transition metal elements.

18 . The method according to claim 16 , wherein the indium dopant precursor comprises In 2 O 3 .

Assignments (1)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jun 22, 2023
From: CHUNG, SUNG-YOON; AN, JI-SANG
To: KOREA ADVANCED INSTITUTE OF SCIENCE AND TECHNOLOGY
Reel/Frame 064031/0808 →
Priority Claims (1)
KR 10-2022-0174198 · Dec 13, 2022 · national
Continuity (1)
Related Publication 20240194407A1 · Jun 13, 2024
References Cited (24)
US 4425556A · Hanke · 1984 [cited by examiner]
US 11805699B2 · Song · 2023 [cited by examiner]
US 20060088719A1 · Ito · 2006 [cited by examiner]
US 20070181846A1 · Liufu · 2007 [cited by examiner]
US 20080009572A1 · Khatua · 2008 [cited by examiner]
US 20120279856A1 · Medvedovski · 2012 [cited by examiner]
US 20170372841A1 · Kawamura · 2017 [cited by examiner]
US 20190148042A1 · Yun · 2019 [cited by examiner]
US 20210098676A1 · Song · 2021 [cited by examiner]
US 20210347697A1 · Badding · 2021 [cited by examiner]
US 20220177371A1 · Chung · 2022 [cited by examiner]
US 20240194407A1 · Chung · 2024 [cited by examiner]
EP 2053028A1 · 2009 [cited by examiner]
JP 9270366A · 1997 [cited by applicant]
KR 1020060052213A · 2006 [cited by applicant]
KR 1020180001463A · 2018 [cited by applicant]
KR 20190074019A · 2019 [cited by examiner]
KR 1020220080549A · 2022 [cited by applicant]
WO WO2022247386A1 · 2022 [cited by examiner]
WO WO2023151685A1 · 2023 [cited by examiner]
Yue Sun, et al., “Effect of Oxygen Vacancy on Electrical Property of Acceptor Doped BaTiO [cited by applicant]
Korean Office Action dated May 9, 2024 in Application No. 10-2022-0174198. [cited by applicant]
M. N. Rahaman et al., “Grain Boundary Mobility of BaTiO3 Doped with Aliovalent Cations”, Journal of the European Ceramic Society, 1998, pp. 1063-1071, vol. 18. [cited by applicant]
Armand J. Atanacio et al., “Effect of Indium Segregation on the surface versus Bulk Chemistry for Indium-Doped TiO2”, Applied Materials & Interfaces, 2012, pp. 6626-6634, vol. 4. [cited by applicant]