Weather-resistant, fungal-resistant, and stain-resistant coatings and methods of applying on wood, masonry, or other porous materials
A process for manufacturing the composition coating may include selecting a wood or masonry material substrate and utilizing a sol-gel comprising a silane or silane derivative and metal oxide precursor to coat the substrate. The process may utilize an all solution process or controlled environment for manufacturing a composition coating that prevent wetting and/or staining of a substrate. The composition coatings for treating wood or masonry materials improves weather-resistance, microbial resistance, stain-resistance and fungal-resistance of the materials. The reduced permeability of the resulting masonry materials can also delay or inhibit degradation caused by permeation of ions such as chlorides and sulfates. In addition, a stain comprising the composite solution and pigments may impart additional property to wood or masonry materials whilst retaining or improving the original appearance, particularly for the visibility and contrast of the wood grain as seen after the application of the coating.
1 . A composite solution comprising:
water;
an acid;
a water-free first solvent comprising methanol;
a base chemical reagent comprising tetraethyl orthosilicate;
a plasticizer comprising trimethoxypropylsilane; and
a bonding agent comprising 3-glycidoxypropyltrimethoxysilane,
wherein the composite solution comprises:
3-8 vol. % of water, 20-30 vol. % of the first solvent, 40-60 vol. % of the base chemical reagent, 10-15 vol. % of the plasticizer, and 1-5 vol. % of the bonding agent, based on 100 vol. % of the composite solution.
2 . The composite solution of claim 1 , wherein the composite solution is prepared by stirring at an elevated temperature in a range of 50-100° C.
3 . The composite solution of claim 2 , wherein the composite solution is stirred at the elevated temperature for ½ hour to 12 hours.
4 . The composite solution of claim 1 , wherein the composite solution is utilized to coat a substrate that is a porous material.
5 . The composite solution of claim 4 , wherein the porous material is selected from wood or masonry material.
6 . The composite solution of claim 1 , wherein the composite solution is prepared under acidic condition with a pH of equal to or less than 5.
7 . The composite solution of claim 1 , wherein a coating formed with the composite solution does not change the pigmentation and reflectivity of the substrate before coating.
8 . The composite solution of claim 1 , wherein the first solvent further comprises at least one of ethanol, n-propanol, isopropanol, n-butanol, isobutanol, ethylene glycol, glycerol acetone, acetonitrile, dioxane, tetrahydrofuran, dimethylformamide, dimethyl sulfoxide or a mixture thereof.
9 . The composite solution of claim 1 , wherein the composite solution further comprises a chelating agent, wherein the chelating agent is selected from an alkoxysilane, metal oxide precursor, or a combination thereof having a general formula of M(OR) x R′ y R″ z (M=Si, Al, In, Sn or Ti; x is the integer 1, 2 or 3; y is the integer 0, 1 or 2; z is the integer 1, 2 or 3, provided that the sum of x, y and z equals 4), where R comprises hydrogen, a substituted or unsubstituted alkyl or derivatives thereof; R′ comprises hydrogen, a substituted or unsubstituted alkyl or derivatives thereof and R″ comprises a substituted or unsubstituted alky or alkenyl group comprising from 3 to 20 carbon atoms, or
the chelating agent is selected from an alkoxysilane, metal oxide precursor, or a combination thereof having a general formula of M(OR) x R′ y R″ z (M=Si, Al, In, Sn or Ti; x is the integer 1, 2 or 3; y is the integer 0, 1 or 2; z is the integer 1, 2 or 3, provided that the sum of x, y and z equals 4), where R comprises hydrogen, a substituted or unsubstituted alkyl or derivatives thereof; R′ comprises hydrogen, a substituted or unsubstituted alkyl or derivatives thereof and R″ comprises a substituted or unsubstituted amine (including primary, secondary and tertiary) or thiol.
10 . The composite solution of claim 1 , wherein the composite solution is for a substrate to improve soil-resistance, stain-resistance, weather-resistance, or fungal-resistance.