Forged carbon fiber rifle barrel
A method of forming a carbon fiber rifle barrel may include the steps of heating a barrel core to increase the length of the barrel, placing the barrel core inside a mold and holding the lengthened barrel in place, adding a carbon fiber mix to the mold in which the carbon fiber mix includes a blend of resin and chopped carbon fibers, sealing the mold, curing the carbon fiber mix surrounding the lengthened barrel core in which the cured carbon fiber mix holds the length of the barrel core creating a tension on the cooled barrel core which increases a rigidity of the rifle barrel thereby increasing the accuracy of the rifle barrel, removing the rifle barrel from the mold, and finishing the rifle barrel via grinding to a desired finish.
1 . A method of forming a rifle barrel comprising the steps of:
heating a barrel core, wherein the heating increases a length of the barrel core;
placing the barrel core inside a mold and holding the lengthened barrel core in tension;
adding a carbon fiber mix to the mold, wherein the carbon fiber mix comprises a blend of resin and chopped carbon fibers;
sealing the mold;
curing the carbon fiber mix surrounding the barrel core, wherein the cured carbon fiber mix holds the tension on the barrel core, and wherein the tension increases a rigidity of the rifle barrel;
removing the rifle barrel from the mold; and
finishing the rifle barrel via grinding to a desired finish.
2 . The method of claim 1 , wherein the barrel core comprises steel.
3 . The method of claim 1 , wherein the chopped carbon fibers comprise non-continuous forged carbon fibers.
4 . The method of claim 1 , wherein an x-ray detectable material is embedded in the carbon fiber mix.
5 . The method of claim 1 , wherein reinforcing fibers are placed around the barrel core prior to adding the carbon fiber mix to the mold.
6 . The method of claim 1 , wherein the mold is subjected to vacuum pressure during curing.
7 . The method of claim 1 , wherein finishing comprises centerless grinding.
8 . The method of claim 1 , further comprising the step of applying a protective wax coating to the finished rifle barrel.
9 . A method of forming a rifle barrel comprising the steps of:
heating a barrel core to grow a length of the barrel core;
placing the barrel core or a mandrel comprising the barrel core inside a mold;
holding the length of the heated barrel core in place;
adding a carbon fiber mix to the mold to surround the barrel core, wherein the carbon fiber mix comprises a blend of resin and carbon fibers;
sealing the mold;
curing the carbon fiber mix, wherein the cured carbon fiber mix holds the length of the barrel core in place causes a tension on the barrel core when the barrel core cools, and wherein the tension increases a rigidity of the rifle barrel;
removing the rifle barrel from the mold; and
finishing the rifle barrel via grinding to a desired finish.
10 . The method of claim 9 , wherein the barrel core is heated to a temperature between 200° F. and 600° F.
11 . The method of claim 9 , wherein the barrel core is made of an alloy selected for high thermal expansion properties.
12 . The method of claim 9 , wherein the carbon fiber mix comprises continuous carbon fibers oriented to enhance rigidity.
13 . The method of claim 9 , wherein the tension created on the barrel core improves barrel harmonics.
14 . The method of claim 9 , wherein the mold is pre-coated with a release agent before the carbon fiber mix is added.
15 . The method of claim 9 , further comprising the step of wrapping the cured rifle barrel with a compression tape before finishing.
16 . The method of claim 9 , wherein curing is temperature controlled to achieve a specific rifle barrel core length contraction rate.
17 . The method of claim 9 , wherein the mold is subjected to autoclave curing for improved bonding.
18 . The method of claim 9 , wherein the barrel core is pre-treated with an adhesion-promoting primer.
19 . A method of forming a rifle barrel consisting of:
heating a barrel core to grow a length of the barrel core;
placing a barrel core inside a mold and holding the heated barrel core length in place;
adding a carbon fiber mix to the mold, wherein carbon fiber mix surrounds the barrel core wherein the carbon fiber mix comprises a blend of resin and carbon fibers;
sealing the mold;
curing the carbon fiber mix, wherein the cured carbon fiber mix holds the length of the barrel core creating a tension on the barrel core when the length of the barrel core decreases due to cooling, and wherein the tension increases a rigidity of the rifle barrel;
removing the rifle barrel from the mold; and
finishing the rifle barrel.
20 . A replacement rifle barrel kit for a firearm comprising the rifle barrel of claim 19 .