Filled skutterudites for advanced thermoelectric applications
A low-cost filled skutterudite for advanced thermoelectric applications is disclosed. The filled skutterudite uses the relatively low-cost mischmetal, either alone or in addition to rare earth elements, as a starting material for guest or filler atoms.
1. A method of fabricating a filled skutterudite for thermoelectric applications, comprising:
providing mischmetal as a starting material for guest atoms in a filled skutterudite, wherein mischmetal comprises at least two rare earth elements and one or more non-rare earth impurities;
providing a source of transition metal atoms (M) and a source of atoms from groups IVA-VIA of the periodic table (X), the respective M and X atoms being in proportion to form a M 4 X 12 skutterudite; and
forming said mischmetal, said source of transition metal atoms and said source of atoms from groups IVA-VIA of the periodic table into a mischmetal filled skutterudite having a chemical composition of Mm y M 4 X 12 , where Mm represents guest atoms of mischmetal; y is a filling fraction of said mischmetal; M represents said transition metal atoms; and X represents said atoms from groups IVA-VIA of the periodic table.
2. The method of claim 1 wherein said chemical composition is Mm y Co 4 Sb 12 (0<y≦1).
3. The method of claim 1 wherein M is Co, Rh or Ir.
4. The method of claim 1 wherein X is P, As or Sb.
5. The method of claim 1 further comprising providing a rare earth element, in addition to said mischmetal, as a starting material for said guest atoms.
6. The method of claim 5 wherein said rare earth element is selected from the group consisting of Ce, Pr, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, Lu, and combinations thereof.
7. The method of claim 1 further comprising:
providing said mischmetal, said source of transition metal atoms and said source of atoms from groups IVA-VIA of the periodic table in powder form;
forming a precursor pellet consisting essentially of said mischmetal powder and said transition metal atoms powder;
mixing said precursor pellet with said powered source of atoms from groups IVA-VIA of the periodic table to form a mixture;
sintering said mixture;
annealing said mixture; and
hot-pressing said mixture to form said filled skutterudite.
8. The method of claim 7 further comprising providing a rare earth element, in addition to said mischmetal, as a starting material for said guest atoms.
9. The method of claim 8 wherein said rare earth element is selected from the group consisting of Ce, Pr, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, Lu, and combinations thereof.