Dirt pick-up resistant composition
Water-based compositions that are resistant to dirt pickup, efflorescence, tannin bleed-through and surfactant leaching are described. The water-based composition includes a latex or water-dispersible polymer and a non-VOC UV-VIS (preferably, ultraviolet) absorber as a dirt pickup resistance additive. Methods of making water-based compositions including a non-VOC UV-VIS absorber as an additive are also described.
1. A water-based coating composition, comprising:
a latex polymer formed from reactants comprising diacetone acrylamide; and
methyl-o-benzoyl benzoate;
wherein the latex polymer is formed from reactants comprising diacetone acrylamide in an amount of no more than 10 wt-%.
2. The composition of claim 1 wherein the latex polymer is a multi-stage latex polymer.
3. The composition of claim 2 wherein the latex polymer has at least one Tg within a range of −10° C. to 40° C.
4. The composition of claim 1 wherein methyl-o-benzoyl benzoate is present in an amount of at least 0.1 wt-% and up to 5.0 wt-%, based on the weight of the polymer solids.
5. The composition of claim 1 wherein the latex polymer is present in the coating composition in an amount of at least 10 wt-%, based on 10-25% solids of the paint for flats and 15-35% for semi-gloss paints.
6. The composition of claim 1 wherein the composition is a water-based paint, sealer, caulk, or sealant.
7. The composition of claim 6 wherein the composition is a water-based paint.
8. The composition of claim 7 wherein the composition is a water-based paint with a pigment volume concentration of 35 to 75 for a flat paint, 20 to 40 for a semi-gloss paint, and about 10 to 25 for a high gloss paint.
9. The composition of claim 7 wherein the composition is a semi-gloss paint having a paint finish that has a moderately satin-like luster and a 60° gloss rating of at least about 30 units.
10. The composition of claim 7 wherein the composition is a high-gloss paint having a paint finish that has a shiny appearance and a 60° gloss rating of at least about 70 units.
11. The composition of claim 1 wherein the composition has extractables of less than about 0.3%.
12. The composition of claim 11 wherein the composition has extractables of less than about 0.2%.
13. The composition of claim 1 wherein the composition includes no greater than 5 grams total VOC per 100 grams polymer solids.
14. The composition of claim 12 further comprising one or more low VOC coalescents having a volatile organic content of 30% or less.
15. A water-based coating composition, comprising:
a multi-stage latex polymer formed from reactants comprising diacetone acrylamide; and
methyl-o-benzoyl benzoate;
wherein the composition includes no greater than 5 grams total VOC per 100 grams polymer solids.
16. The composition of claim 15 wherein the latex polymer has at least one Tg within a range of −10° C. to 40° C.
17. The composition of claim 15 wherein methyl-o-benzoyl benzoate is present in an amount of at least 0.1 wt-% and up to 5.0 wt-%, based on the weight of the polymer solids.
18. The composition of claim 15 wherein the latex polymer is present in the coating composition in an amount of at least 10 wt-%, based on 10-25% solids of the paint for flats and 15-35% for semi-gloss paints.
19. The composition of claim 15 wherein the latex polymer is formed from reactants comprising diacetone acrylamide in an amount of no more than 10 wt-%.