Dual catalyst system for producing polyethylene with long chain branching for blow molding applications
Ethylene-based polymers are characterized by a melt index less than 1 g/10 min, a density from 0.94 to 0.965 g/cm 3 , a Mw from 100,000 to 250,000 g/mol, a relaxation time from 0.5 to 3 sec, and an average number of long chain branches (LCBs) per 1,000,000 total carbon atoms in a molecular weight range of 300,000 to 900,000 g/mol that is greater than that in a molecular weight range of 1,000,000 to 2,000,000 g/mol, or an average number of LCBs per 1,000,000 total carbon atoms in a molecular weight range of 1,000,000 to 2,000,000 g/mol of less than or equal to about 5 and a maximum ratio of η E /3η at an extensional rate of 0.1 sec −1 from 1.2 to 10. These polymers have substantially no long chain branching in the high molecular weight fraction of the polymer, but instead have significant long chain branching in a lower molecular weight fraction, such that polymer melt strength and parison stability are maintained for the fabrication of blow molded products and other articles of manufacture. These ethylene polymers can be produced using a dual catalyst system containing a single or two atom bridged metallocene compound with two indenyl groups, and a single atom bridged metallocene compound with a fluorenyl group and a cyclopentadienyl group.
1. An ethylene polymer having:
a melt index of less than or equal to about 1 g/10 min;
a density in a range from about 0.94 to about 0.965 g/cm 3 ;
a Mw in a range from about 100,000 to about 250,000 g/mol;
a relaxation time from about 0.5 to about 3 sec; and
an average number of long chain branches (LCBs) per 1,000,000 total carbon atoms of the ethylene polymer in a molecular weight range of 300,000 to 900,000 g/mol that is greater than that in a molecular weight range of 1,000,000 to 2,000,000 g/mol.
2. An article of manufacture comprising the ethylene polymer of claim 1 .
3. The ethylene polymer of claim 1 , wherein:
the melt index is in a range from about 0.1 to about 0.5 g/10 min;
the density is in a range from about 0.94 to about 0.96 g/cm 3 ;
the average number of LCBs per 1,000,000 total carbon atoms of the ethylene polymer in the molecular weight range of 300,000 to 900,000 g/mol is at least 100% greater than that in the molecular weight range of 1,000,000 to 2,000,000 g/mol; and
the ethylene polymer comprises an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, an ethylene/1-octene copolymer, or a combination thereof.
4. A blow molded product comprising the ethylene polymer of claim 3 .
5. The ethylene polymer of claim 3 , wherein the ethylene polymer has:
a CY-a parameter in a range from about 0.2 to about 0.4; and
a relaxation time in a range from about 0.75 to about 2.5 sec.
6. The ethylene polymer of claim 3 , wherein the ethylene polymer has:
an environmental stress crack resistance (ESCR, ASTM D2561) of at least 200 hours; and
an environmental stress crack resistance (ESCR, ASTM D1693) of at least 50 hours.
7. The ethylene polymer of claim 1 , wherein the ethylene polymer has:
an average number of from about 3 to about 15 LCBs per 1,000,000 total carbon atoms of the ethylene polymer in the molecular weight range of 300,000 to 900,000 g/mol; and/or
an average number of from about 4 to about 15 LCBs per 1,000,000 total carbon atoms of the ethylene polymer in a molecular weight range of 400,000 to 600,000 g/mol.
8. The ethylene polymer of claim 7 , wherein the ethylene polymer comprises an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, an ethylene/1-octene copolymer, or a combination thereof.
9. The ethylene polymer of claim 8 , wherein the Mw is in a range from about 110,000 to about 190,000 g/mol.
10. The ethylene polymer of claim 8 , wherein the ethylene polymer has:
a ratio of Mw/Mn in a range from about 6 to about 12; and
a ratio of Mz/Mw in a range from about 4 to about 8.
11. An ethylene polymer having:
a melt index of less than or equal to about 1 g/10 min;
a density in a range from about 0.94 to about 0.965 g/cm 3 ;
a Mw in a range from about 100,000 to about 250,000 g/mol;
a relaxation time from about 0.5 to about 3 sec;
an average number of long chain branches (LCBs) per 1,000,000 total carbon atoms of the ethylene polymer in a molecular weight range of 1,000,000 to 2,000,000 g/mol of less than or equal to about 5; and
a maximum ratio of extensional viscosity to three times shear viscosity η E /3η at an extensional rate of 0.1 sec −1 in a range from about 1.2 to about 10.
12. An article of manufacture comprising the polymer of claim 11 .
13. The ethylene polymer of claim 11 , wherein:
the average number of LCBs per 1,000,000 total carbon atoms of the ethylene polymer in the molecular weight range of 1,000,000 to 2,000,000 g/mol is less than or equal to about 3.5; and
the maximum ratio of η E /3η at the extensional rate of 0.1 sec −1 is in a range from about 1.5 to about 5.
14. The ethylene polymer of claim 11 , wherein:
the melt index is in a range from about 0.1 to about 0.5 g/10 min;
the density is in a range from about 0.94 to about 0.96 g/cm 3 ; and
the ethylene polymer comprises an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, an ethylene/1-octene copolymer, or a combination thereof.
15. A blow molded product comprising the ethylene polymer of claim 14 .
16. The ethylene polymer of claim 14 , wherein the ethylene polymer has:
a CY-a parameter in a range from about 0.2 to about 0.4; and
a relaxation time in a range from about 0.75 to about 2.5 sec.
17. The ethylene polymer of claim 14 , wherein the ethylene polymer has:
an environmental stress crack resistance (ESCR, ASTM D2561) of at least 200 hours; and
an environmental stress crack resistance (ESCR, ASTM D1693) of at least 50 hours.
18. The ethylene polymer of claim 14 , wherein the ethylene polymer contains from about 5 to about 15 LCBs per 1,000,000 total carbon atoms.
19. The ethylene polymer of claim 14 , wherein the ethylene polymer has a maximum ratio of η E /3η at an extensional rate of 0.03 sec −1 in a range from about 1.5 to about 8.
20. An olefin polymerization process, the process comprising contacting a catalyst composition with ethylene and an olefin comonomer in a polymerization reactor system under polymerization conditions to produce an ethylene polymer, wherein:
the catalyst composition comprises:
catalyst component I comprising a single atom bridged or two atom bridged metallocene compound with two indenyl groups;
catalyst component II comprising a single atom bridged metallocene compound with a fluorenyl group and a cyclopentadienyl group, and with an alkenyl substituent on the single atom bridge and/or on the cyclopentadienyl group;
an activator; and
optionally, a co-catalyst; and
the ethylene polymer is characterized by:
a melt index of less than or equal to about 1 g/10 min;
a density in a range from about 0.94 to about 0.965 g/cm 3 ;
a Mw in a range from about 100,000 to about 250,000 g/mol;
a relaxation time from about 0.5 to about 3 sec; and
an average number of LCBs per 1,000,000 total carbon atoms of the polymer in a molecular weight range of 300,000 to 900,000 g/mol that is greater than that in a molecular weight range of 1,000,000 to 2,000,000 g/mol.