Plasma etching method using gas molecule containing sulfur atom
Provided is a plasma etching method that enables, in a semiconductor fabrication process, selective processing of a film consisting of a single material, such as SiO 2 or SiN, or a composite material of SiO 2 and SiN over a mask material as well as processing into satisfactorily vertical processed shapes. It is possible, for example, to enhance selectivity over a mask material or other materials excluding an etching target, to reduce damage on sidewalls, and to suppress etching in the lateral direction by generating a plasma of a gas compound having a thioether skeleton represented by general formula (1) or a mixed gas thereof and etching a film consisting of a composite material or a single material, such as SiO 2 or SiN, thereby depositing a protective film that contains sulfur atoms and has a lower content of fluorine atoms than the cases of using common hydrofluorocarbon gases: general formula (1): Rf 1 —S—Rf 2 (1) where Rf 1 is a monovalent organic group represented by C x H y F z and Rf 2 is a monovalent organic group represented by C a H b F c .
1. A method of etching a Si-containing film, comprising dry etching a Si-containing film with a gas plasma containing CH 3 —S—CF 3 .
2. The method according to claim 1 , wherein the Si-containing film is a single-layer film comprising one material containing Si or a multilayer film of stacked two or more materials containing Si.
3. The method according to claim 1 , wherein the gas plasma contains, in addition to the compound represented by general formula (1), at least one selected from the group consisting of HF, HCl, HBr, HI, CF 4 , CHF 3 , CH 2 F 2 , CH 3 F, COF 2 , C 2 F 6 , C 3 F 6 , C 3 F 8 , C 4 F 8 , C 4 F 6 , C 5 F 8 , NF 3 , and SF 6 .
4. The method according to claim 1 , wherein:
the Si-containing film constitutes, together with a material that is not to be etched, a structure; and
a film that contains S but has F content of 1% or less is deposited on a surface of the structure during etching.
5. The method according to claim 1 , wherein the Si-containing film is a film comprising at least one material selected from the group consisting of SiO 2 , SiN, SiON, SiCN, SiOC, and SiOCN.
6. The method according to claim 4 , wherein the material that is not to be etched is at least one selected from the group consisting of an amorphous carbon layer (ACL), spin-on carbon (SOC), TiN, TaN, and photoresists.
7. The method according to claim 1 , wherein the gas plasma further contains at least one selected from the group consisting of N 2 , O 2 , O 3 , CO, CO 2 , COS, N 2 O, NO, NO 2 , SO 2 , and SO 3 .
8. The method according to claim 1 , wherein the gas plasma further contains at least one selected from the group consisting of H 2 , NH 3 , and SiH 4 .
9. The method according to claim 1 , wherein the gas plasma further contains at least one selected from the group consisting of He, Ar, Ne, Kr, and Xe.