Ethylene/alpha-olefin copolymer and method for preparing the same
The present invention relates to an ethylene/alpha-olefin copolymer having a high weight average molecular weight and narrow molecular weight distribution, and at the same time, a reduced characteristic relaxation time, thereby showing excellent physical properties, and a method for preparing the same. A resin composition having improved volume resistance and excellent light transmittance may be prepared by using such ethylene/alpha-olefin copolymer. Accordingly, the ethylene/alpha-olefin copolymer may be utilized in various uses in electrical and electronic industrial fields.
1. An ethylene/alpha-olefin copolymer satisfying the following conditions (a) to (c):
(a) a characteristic relaxation time at 190° C. in shear rate conditions of 0.1 to 500 rad/s, is less than 10.0 millisecond;
(b) a weight average molecular weight is from 40,000 to 150,000 g/mol; and
(c) a molecular weight distribution is from 1.5 to 2.5,
wherein the ethylene/alpha-olefin copolymer has a density from 0.850 to 0.910 g/cc.
2. The ethylene/alpha-olefin copolymer according to claim 1 ,
wherein the characteristic relaxation time is from 1.0 to 9.5 millisecond.
3. The ethylene/alpha-olefin copolymer according to claim 1 , wherein the weight average molecular weight is from 41,000 to 130,000 g/mol.
4. The ethylene/alpha-olefin copolymer according to claim 1 , wherein the molecular weight distribution is from 1.5 to 2.4.
5. The ethylene/alpha-olefin copolymer according to claim 1 , which has a melt index (190° C., 2.16 kg load conditions) from 0.1 to 50 g/10 min.
6. The ethylene/alpha-olefin copolymer according to claim 1 , wherein the alpha-olefin comprises one or more of propylene, 1-butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-heptene, 1-octene, 1-decene, 1-undecene, 1-dodecene, 1-tetradecene, 1-hexadecene or 1-eicosene.
7. A method for preparing the ethylene/alpha-olefin copolymer of claim 1 , the method comprising:
(S1) a step of preparing a polymerization product of ethylene and an alpha-olefin monomer;
(S2) a step of dissolving the polymerization product in an organic solvent; and
(S3) a step of mixing with an alcohol of 2 to 5 carbon atoms to form the ethylene/alpha-olefin copolymer as a precipitate.
8. The method of claim 7 , wherein the organic solvent is a compound having 7 to 16 carbon atoms.
9. The method of claim 7 , wherein the organic solvent is one or more selected from the group consisting of heptane, octane, isooctane, toluene, xylene and cumene.
10. The method of claim 7 , wherein the alcohol having 2 to 5 carbon atoms is one or more selected from the group consisting of ethanol, propan-1-ol, propan-2-ol, butan-1-ol, butan-2-ol, 2-methylpropan-2-ol, pentan-1-ol, pentan-2-ol, pentan-3-ol, 2-methylbutan-2-ol and 3-methylbutan-2-ol.
11. The method of claim 7 , wherein the step (S2) and the step (S3) are alternately repeatedly performed by twice to five times.
12. An encapsulant film comprising an ethylene/alpha-olefin copolymer satisfying the following conditions (a) to (c):
(a) a characteristic relaxation time at 190° C. in shear rate conditions of 0.1 to 500 rad/s, is less than 10.0 millisecond;
(b) a weight average molecular weight is from 40,000 to 150,000 g/mol; and
(c) a molecular weight distribution is from 1.5 to 2.5,
wherein the ethylene/alpha-olefin copolymer has a density from 0.850 to 0.910 g/cc.
13. The encapsulant film according to claim 12 , further comprising one or more of a crosslinking agent, a crosslinking auxiliary agent, a silane coupling agent, an unsaturated silane compound, an amino silane compound, a light stabilizer, a UV absorbent or a thermal stabilizer.
14. A solar cell module comprising the encapsulant film of claim 12 .