Platinum nanoparticle deposition on a series of UiO metal-organic frameworks
Deposition of Pt nanoparticles on UiO metal organic frameworks via solvothermal reduction is achieved by reducing Pt acetylacetonate (Pt(acac) 2 ) in a UiO-66 and N,N-dimethylformamide (DMF) mixture at, for example, 130° C. for 18 hrs. Modification of reaction temperature and time can control the size of the Pt nanoparticles.
1. A method of depositing platinum nanoparticles onto a metal organic framework (MOF), the method comprising:
providing a MOF in N,N-dimethylformamide (DMF); and
contacting the MOF with platinum acetylacetonate at a temperature between 100° C. and 180° C., thereby depositing platinum nanoparticles onto the MOF.
2. The method of claim 1 , wherein said MOF is UiO-66.
3. The method of claim 1 , wherein said temperature is between 120° C. and 150° C.
4. The method of claim 1 , wherein said depositing is accomplished as a single reaction to produce said platinum nanoparticles deposited onto the MOF without a need for additional steps.
5. A method of depositing platinum nanoparticles onto a metal organic framework (MOF), the method consisting essentially of:
providing a MOF in N,N-dimethylformamide (DMF); and
contacting the MOF with platinum acetylacetonate at a temperature between 100° C. and 180° C., thereby depositing platinum nanoparticles onto the MOF.
6. The method of claim 4 , wherein said MOF is UiO-66.
7. The method of claim 4 , wherein said temperature is between 120° C. and 150° C.