Method for flattening a surface on an epitaxial lateral growth layer
View Patent ↗A method for flattening a surface on an epitaxial lateral overgrowth (ELO) layer, resulting in obtaining a smooth surface with island-like III-nitride semiconductor layers. The island-like III-nitride semiconductor layers are formed by stopping the growth of the ELO layers before they coalesce to each other. Then, a growth restrict mask is removed before at least some III-nitride device layers are grown. Removing the mask decreases an excess gases supply to side facets of the island-like III-nitride semiconductor layers, which can help to obtain a smooth surface on the island-like III-nitride semiconductor layers. The method also avoids compensation of a p-type layer by decomposed n-type dopant from the mask, such as Silicon and Oxygen atoms.
1. A method for manufacturing a semiconductor layer, comprising:
preparing a plurality of epitaxial lateral overgrowth (ELO) III-nitride layers grown on or above a growth restrict mask on a substrate, wherein adjacent ones of the plurality of ELO III-nitride layers are separated from each other by a no-growth region;
removing of the growth restrict mask in the no-growth region, wherein the growth restrict mask does not remain between adjacent ones of the plurality of ELO III-nitride layers and a portion of the growth restrict mask remains between the substrate and the plurality of ELO III-nitride layers; and
growing a plurality of III-nitride device layers on or above the plurality of ELO III-nitride layers and the substrate, wherein adjacent ones of the plurality of III-nitride device layers are separated from each other by the no-growth region;
wherein:
the growth restrict mask is removed after growing the plurality of ELO III-nitride layers and before growing at least some of the plurality of III-nitride device layers; and
the plurality of ELO III-nitride layers are grown to a height that prevents growth of a bottom layer in the no-growth region where the growth mask is removed, during the growth of the III-nitride device layers.
2. The method of claim 1 , wherein the III-nitride device layers include a p-type layer.
3. The method of claim 1 , wherein at least a part of the growth restrict mask is removed where the growth restrict mask is not covered by the ELO III-nitride layers.
4. The method of claim 1 , wherein the III-nitride device layers include a low-temperature growth layer, an Indium-containing layer, an Aluminum-containing layer, and/or a p-type layer, and the growth restrict mask is removed before growing the low-temperature growth layer, Indium-containing layer, Aluminum-containing layer, and/or p-type layer.
5. The method of claim 4 , wherein the growth restrict mask is removed before growing the p-type layer to avoid compensation of the p-type layer due to decomposition of the growth restrict mask.
6. The method of claim 1 , wherein the growth restrict mask is removed before growing at least an active layer of the III-nitride device layers.
7. The method of claim 1 , wherein the ELO III-nitride layers and the III-nitride device layers together comprise island-like III-nitride semiconductor layers, and adjacent ones of the island-like III-nitride semiconductor layers are separated from each other by the no-growth region.