Silica wet gel and aerogel
The invention provides silica wet gel, silica aerogel, and methods that can be used to form an enhanced silica aerogel sheet having fewer optical defects along with other desirable properties.
1 . An article comprising a glass substrate and a silica aerogel sheet, the silica aerogel sheet being adhered to the glass substrate and being formed from a precursor material comprising methyl silicate 51 and having a thickness in a range of from 1.5 to 15 mm, a haze of less than 2.5%, a visible transmission of greater than 98%, a thermal conductivity of less than 20 mW/m*K, and a global structural similarity index measure of greater than 0.80, wherein the silica aerogel sheet is self-supporting such that the silica aerogel sheet retains sheet form without being adhered to a substrate.
2 . The article of claim 1 wherein the haze of the silica aerogel sheet is less than 1.75%.
3 . The article of claim 1 wherein the thermal conductivity of the silica aerogel sheet is less than 13 mW/m*K.
4 . The article of claim 1 wherein the silica aerogel sheet is devoid of structural non-uniformities that create optical distortion lines visible to the naked eye.
5 . The article of claim 1 wherein the silica aerogel sheet is prepared by a method comprising the steps of:
preparing a first solution by mixing methyl silicate 51 and methanol;
preparing a second solution by mixing ammonium hydroxide and water;
mixing the first solution and the second solution together to form a precursor material; allowing components in the precursor material to react to form silica wet gel; and
depositing the silica wet gel onto a substrate to form a silica wet gel sheet; and
drying the silica wet gel sheet to form the silica aerogel sheet.
6 . The article of claim 5 wherein the precursor material has a weight percent ratio of the methyl silicate 51:water of between 0.25:1 and 2:1.
7 . The article of claim 6 wherein the weight percent ratio of the methyl silicate 51:water for the precursor material is between 0.5:1 and 1:1.
8 . The article of claim 5 wherein the precursor material comprises:
methyl silicate 51 at a weight percent of greater than or equal to 15% and less than or equal to or equal to 24%;
methanol at a weight percent of greater than or equal to 60% and less than or equal to 68%;
water at a weight percent of greater than or equal to 15% and less than or equal to 17%; and
ammonium hydroxide at a weight percent of greater than or equal to 0.08% and less than or equal to 0.2%.
9 . The article of claim 8 wherein the precursor material comprises:
methyl silicate 51 at a weight percent of greater than or equal to 15.28% and less than or equal to 19%;
methanol at a weight percent of greater than or equal to 65.16% and less than or equal to 68.52%;
water at a weight percent of greater than or equal to 15.68% and less than or equal to 16.04%; and
ammonium hydroxide at a weight percent of greater than or equal to 0.15% and less than or equal to 0.17%.
10 . The article of claim 5 wherein the precursor material is devoid of N,N-dimethylformamide.
11 . An insulating glazing unit comprising two glass sheets and a between-pane space, the between-pane space being located between the two glass sheets, the insulating glazing unit further comprising a silica aerogel sheet received in the between-pane space, the silica aerogel sheet being formed from a precursor material comprising methyl silicate 51 and having a thickness in a range of from 1.5 to 15 mm, a haze of less than 2.5%, a visible transmission greater than 98%, a thermal conductivity of less than 20 mW/m*K, and a global structural similarity index measure of greater than 0.80, wherein the silica aerogel sheet is self-supporting such that the silica aerogel sheet retains sheet form without being adhered to a substrate.
12 . The insulating glazing unit of claim 11 wherein the haze of the silica aerogel sheet is less than 1.75%.
13 . The insulating glazing unit of claim 11 wherein the thermal conductivity of the silica aerogel sheet is less than 10 mW/m*K.
14 . The insulating glazing unit of claim 11 wherein the silica aerogel sheet is adhered to an interior surface of one of the two glass sheets.
15 . The insulating glazing unit of claim 11 wherein the silica aerogel sheet is adhered to an interior surface of one of the two glass sheets and a low-emissivity coating is provided on an interior surface of the other of the two glass sheets.
16 . The insulating glazing unit of claim 11 wherein the silica aerogel sheet is devoid of structural non-uniformities that create optical distortion lines visible to the naked eye.
17 . The insulating glazing unit of claim 11 wherein the insulating glazing unit is prepared by a method comprising the steps of:
preparing a first solution by mixing methyl silicate 51 and methanol;
preparing a second solution by mixing ammonium hydroxide and water;
mixing the first solution and the second solution together to form a precursor material;
allowing components in the precursor material to react to form silica wet gel;
depositing the silica wet gel onto a substrate to form a silica wet gel sheet;
drying the silica wet gel sheet to form the silica aerogel sheet; and
assembling the silica aerogel sheet together with the two glass sheets in forming the insulating glazing unit.
18 . The insulating glazing unit of claim 17 wherein the precursor material has a weight percent ratio of the methyl silicate 51:water of between 0.25:1 and 2:1.
19 . The insulating glazing unit of claim 18 wherein the weight percent ratio of the methyl silicate 51:water for the precursor material is between 0.5:1 and 1:1.
20 . The insulating glazing unit of claim 17 wherein the precursor material comprises:
methyl silicate 51 at a weight percent of greater than or equal to 15% and less than or equal to or equal to 24%;
methanol at a weight percent of greater than or equal to 60% and less than or equal to 68%;
water at a weight percent of greater than or equal to 15% and less than or equal to 17%; and
ammonium hydroxide at a weight percent of greater than or equal to 0.08% and less than or equal to 0.2%.
21 . The insulating glazing unit of claim 20 wherein the precursor material comprises:
methyl silicate 51 at a weight percent of greater than or equal to 15.28% and less than or equal to 19%;
methanol at a weight percent of greater than or equal to 65.16% and less than or equal to 68.52%;
water at a weight percent of greater than or equal to 15.68% and less than or equal to 16.04%; and
ammonium hydroxide at a weight percent of greater than or equal to 0.15% and less than or equal to 0.17%.
22 . The insulating glazing unit of claim 17 wherein the precursor material is devoid of N,N-dimethylformamide.
23 . A laminated glass assembly comprising two glass sheets and a silica aerogel sheet between the two glass sheets, the silica aerogel sheet being formed from a precursor material comprising methyl silicate 51 and having a thickness in a range of from 1.5 to 15 mm, a haze of less than 2.5%, a visible transmission of greater than 98%, a thermal conductivity of less than 20 mW/m*K, and a global structural similarity index measure of greater than 0.80, wherein the silica aerogel sheet is self-supporting such that the silica aerogel sheet retains sheet form without being adhered to a substrate.
24 . The laminated glass assembly of claim 23 wherein the haze of the silica aerogel sheet is less than 1.75%.
25 . The laminated glass assembly of claim 23 wherein the thermal conductivity of the silica aerogel sheet is less than 13 mW/m*K.
26 . The laminated glass assembly of claim 23 wherein the silica aerogel sheet is adhered to both of the two glass sheets.
27 . The laminated glass assembly of claim 23 wherein the silica aerogel sheet is devoid of structural non-uniformities that create optical distortion lines visible to the naked eye.
28 . The laminated glass assembly of claim 23 wherein the laminated glass assembly is prepared by a method comprising the steps of:
preparing a first solution by mixing methyl silicate 51 and methanol;
preparing a second solution by mixing ammonium hydroxide and water;
mixing the first solution and the second solution together to form a precursor material;
allowing components in the precursor material to react to form a silica wet gel;
depositing the silica wet gel onto a substrate to form a silica wet gel sheet;
drying the silica wet gel sheet to form the silica aerogel sheet; and
assembling the silica aerogel sheet together with the two glass sheets in forming the laminated glass assembly.
29 . The laminated glass assembly of claim 28 wherein the precursor material has a weight percent ratio of the methyl silicate 51:water of between 0.25:1 and 2:1.
30 . The laminated glass assembly of claim 29 wherein the weight percent ratio of the methyl silicate 51:water for the precursor material is between 0.5:1 and 1:1.
31 . The laminated glass assembly of claim 28 wherein the precursor material comprises:
methyl silicate 51 at a weight percent of greater than or equal to 15% and less than or equal to or equal to 24%;
methanol at a weight percent of greater than or equal to 60% and less than or equal to 68%;
water at a weight percent of greater than or equal to 15% and less than or equal to 17%; and
ammonium hydroxide at a weight percent of greater than or equal to 0.08% and less than or equal to 0.2%.
32 . The laminated glass assembly of claim 31 wherein the precursor material comprises:
methyl silicate 51 at a weight percent of greater than or equal to 15.28% and less than or equal to 19%;
methanol at a weight percent of greater than or equal to 65.16% and less than or equal to 68.52%;
water at a weight percent of greater than or equal to 15.68% and less than or equal to 16.04%; and
ammonium hydroxide at a weight percent of greater than or equal to 0.15% and less than or equal to 0.17%.
33 . The laminated glass assembly of claim 28 wherein the precursor material is devoid of N,N-dimethylformamide.