Copper alloy containing cobalt, nickel and silicon
View Patent ↗A copper alloy having an improved combination of yield strength and electrical conductivity consists essentially of, by weight, from 1% to 2.5% of nickel, from 0.5% to 2.0% of cobalt, from 0.5% to 1.5% of silicon, and the balance is copper and inevitable impurities. Further, the total nickel plus cobalt content is from 1.7% to 4.3%, the ratio of nickel to cobalt is from 1.01:1 to 2.6:1, the amount of (Ni+Co)/Si is between 3.5 and 6, the electrical conductivity is in excess of 40% IACS and the yield strength is in excess of 95 ksi. An optional inclusion is up 1% of silver. A process to manufacture the alloy includes the sequential steps of (a). casting; (b). hot working; (c). solutionizing; (d). first age annealing; (e). cold working; and (f). second age annealing wherein the second age annealing temperature is less than the first age annealing temperature.
1. A wrought copper alloy consisting essentially, by weight, of: from 1% to 2.5% of nickel; from 0.5% to 2.0% of cobalt, with a total nickel plus cobalt content of from 1.7% to 4.3% and a weight percent ratio of nickel to cobalt that is from 1.01:1 to 2.6:1; from 0.5% to 1.5% of silicon with the weight ratio of (Ni+Co)/Si being between 3.5:1 and 6:1;
a maximum zinc content of 0.025%;
a maximum chromium content of 0.08%;
a maximum tin content of 0.04%;
a maximum phosphorus content of 0.04%;
a maximum magnesium content of 0.04%;
and the balance copper and inevitable impurities wherein said wrought copper alloy has an electrical conductivity in excess of 40% IACS, a yield strength in excess of 95 ksi, a minimum bend radius as a function of thickness, mbr/t of up to 4 t for both good way and bad way bends and an average grain size of 20 microns or less following solutionizing at 950° C.
2. The wrought copper alloy of claim 1 wherein said nickel content is from 1.3% to 1.9%, said cobalt content is from 0.5% to 1.5% and said silicon content is from 0.5% to 0.8%.
3. The wrought copper alloy of claim 2 wherein a weight percent ratio of nickel to cobalt is from 1.01:1 to 1.5:1.
4. The wrought copper alloy of claim 3 wherein said wrought copper alloy has a yield strength of 100 ksi or greater.
5. A wrought copper alloy consisting essentially, by weight, of: from 1% to 2.5% of nickel; from 0.5% to 2.0% of cobalt, with a total nickel plus cobalt content of from 1.7% to 4.3% and a weight percent ratio of nickel to cobalt that is from 1.01:1 to 2.6:1;
from 0.5% to 1.5% of silicon with the weight ratio of (Ni+Co)/Si being between 3.5:1 and 6:1; from an amount effective to improve a combination of yield strength and electrical conductivity up to 1.0% of silver, titanium, zirconium and combinations thereof; up to
a maximum zinc content of 0.025%;
a maximum chromium content of 0.08%;
a maximum tin content of 0.04%;
a maximum phosphorus content of 0.04%;
up to 0.15% of magnesium; and the balance copper and inevitable impurities wherein said wrought copper alloy has an electrical conductivity in excess of 40% IACS, a minimum bend radius as a function of thickness, mbr/t of up to 4t for both good way and bad way bends and an average grain size of 20 microns or less following solutionizing at 950° C.
6. The wrought copper alloy of claim 5 wherein said silver content is from 0.2% to 0.7%.
7. The wrought copper alloy of claim 6 wherein the magnesium content is between 0.005% and 0.04%.
8. The wrought copper alloy of claim 6 wherein said nickel content is from 1.3% to 1.9%, said cobalt content is from 0.5% to 1.5% and said silicon content is from 0.5% to 0.8%.
9. The wrought copper alloy of claim 8 wherein a weight percent ratio of nickel to cobalt is from 1.01:1 to 1.5:1.
10. The wrought copper alloy of claim 9 wherein said wrought copper alloy has a yield strength of 100 ksi or greater.