Treating sulfide glass surfaces and making solid state laminate electrode assemblies
Methods for making solid-state laminate electrode assemblies include methods of forming a solid electrolyte interphase (SEI) by ion implanting nitrogen and/or phosphorous into the glass surface by ion implantation.
1. A method for making a battery cell, the method comprising:
forming a solid-state laminate electrode assembly by,
providing a lithium ion conducting sulfide glass substrate, the substrate comprising a sulfide glass solid electrolyte sheet having room temperature Li ion conductivity of at least 10 −5 S/cm, the sulfide glass substrate having first and second major surfaces;
injecting nitrogen and/or phosphorous into the first major surface of the sulfide glass substrate, wherein the nitrogen and/or phosphorous penetrates the glass surface forming an implanted zone;
evaporating lithium metal onto the implanted zone of the sulfide glass substrate; wherein at least a portion of the evaporated lithium reacts with the injected nitrogen and/or phosphorous to form a solid electrolyte interphase (SEI) layer comprising lithium and one or both of nitrogen and phosphorous; and
disposing a positive electrode adjacent to the second major surface of the sulfide glass substrate of the solid-state laminate electrode assembly.
2. The method of claim 1 , wherein the implanted zone is substantially uniform and the SEI layer is continuous.
3. The method of claim 1 , wherein the SEI comprises lithium nitride.
4. The method of claim 1 , wherein the SEI comprises lithium phosphide.
5. The method of claim 1 , wherein the SEI is a continuous layer of a lithium nitride and/or lithium phosphide compound.
6. The method of claim 1 , wherein the injecting is performed by ion implantation using a nitrogen and/or phosphorous ion gun.
7. The method of claim 1 , wherein the nitrogen and/or phosphorous ion implantation zone is not greater than 10 nm deep.
8. The method of claim 1 , wherein the nitrogen and/or phosphorous ion implantation zone is not greater than 10-100 nm deep.
9. The method of claim 1 , wherein the nitrogen and/or phosphorous ion implantation zone is not greater than 100-1000 nm deep.
10. The method of claim 1 , wherein the injecting and the lithium evaporation takes place simultaneously.
11. The method of claim 10 , comprising injecting nitrogen and/or phosphorous onto the glass surface prior to lithium evaporation; simultaneously injecting and evaporating lithium metal; and, stopping the nitrogen injection while continuing the evaporation.
12. The method of claim 1 , wherein the positive electrode is a lithium ion intercalating material electrode.
13. The method of claim 12 , wherein the lithium ion intercalating material electrode comprises an intercalating transition metal oxide.
14. The method of claim 13 , wherein the transition metal oxide is selected from the group consisting of lithium cobalt oxides, lithium manganese oxides, lithium nickel oxides, lithium nickel manganese cobalt oxides and lithium nickel cobalt aluminum oxides.
15. The method of claim 1 , wherein a battery electrolyte is disposed between the second major surface of the sulfide glass substrate of the solid-state laminate electrode assembly and the positive electrode.
16. The method of claim 15 , wherein the battery electrolyte is a liquid electrolyte impregnated in porous polymer membrane and/or a gel electrolyte layer.
17. The method of claim 1 , wherein the battery cell is fully solid-state and the positive electrode is disposed in direct contact with the second major surface of the sulfide glass substrate of the solid-state laminate electrode assembly.
18. A battery cell, comprising:
a solid-state laminate electrode assembly comprising,
a lithium ion conducting sulfide glass substrate, the substrate comprising a sulfide glass solid electrolyte sheet having room temperature Li ion conductivity of at least 10 −5 S/cm, the sulfide glass substrate having first and second major surfaces;
a solid electrolyte interphase (SEI) layer comprising lithium and one or both of nitrogen and phosphorous at the first major surface of the sulfide glass substrate; and
a lithium ion intercalating transition metal oxide positive electrode adjacent to the second major surface of the sulfide glass substrate of the solid-state laminate electrode assembly.
19. The battery cell of claim 18 , wherein a battery electrolyte is disposed between the second major surface of the sulfide glass substrate of the solid-state laminate electrode assembly and the positive electrode.
20. The battery cell of claim 18 , wherein the battery cell is fully solid-state and the positive electrode is disposed in direct contact with the second major surface of the sulfide glass substrate of the solid-state laminate electrode assembly.