Methods and systems for scalable direct recycling of battery waste
Embodiments described herein relate to methods of recycling battery waste. In some aspects, a method can include applying a first heat treatment at a temperature of between about 100° C. and about 700° C. to the battery waste, the first heat treatment decomposing at least about 80 wt % of the binder, separating the electrode material from the current collector, and applying a second heat treatment at a temperature between about 400° C. and about 1,200° C. to the electrode material to produce a regenerated electrode material, the second heat treatment decomposing at least 90 wt % of binder remaining in the electrode material to produce a regenerated electrode material. In some embodiments, the method can include applying a surface treatment to the electrode material to remove surface coatings and/or surface impurities from the electrode material. In some embodiments, the surface treatment can include applying a solvent to the electrode material.
1. A method of recycling a quantity of battery waste, the battery waste including an electrode material and a current collector, the electrode material including an active material and a binder, the method comprising:
applying a first heat treatment in an inert or reducing gas environment at a temperature of between about 400° C. and about 600° C. to the battery waste, the first heat treatment decomposing at least about 80 wt % of the binder;
separating the electrode material from the current collector; and
applying a second heat treatment in an inert or a reducing gas environment at a temperature between about 400° C. and about 1,200° C. to the electrode material to produce a regenerated electrode material, the second heat treatment decomposing at least 90 wt % of binder remaining in the electrode material to produce a regenerated electrode material.
2. The method of claim 1 , further comprising:
applying a surface treatment to the electrode material to remove surface coatings and/or surface impurities from the electrode material.
3. The method of claim 2 , wherein the surface treatment includes applying a solvent to the electrode material.
4. The method of claim 3 , wherein the solvent includes at least one of citric acid, acetic acid, oxalic acid, ammonia, ammonium hydroxide, ammonium chloride, or chemical derivatives thereof.
5. The method of claim 1 , wherein
the electrode material includes at least one of LiCoO 2 , LiMn 2 O 4 , LiFe t M 1-t PO 4 , or LiNi a Mn b Co c A d O 2 , wherein
M includes a metal element; wherein
a+b+c+d=1; wherein
0<t<1; and wherein
A=Al, Zr, or Mg.
6. The method of claim 1 , wherein the first heat treatment has a duration of between about 1 hour and about 6 hours, and wherein
the second heat treatment has a duration of between about 1 hour and about 5 hours and a temperature of between about 450° C. and about 800° C.
7. The method of claim 1 , wherein the first heat treatment has a duration of between about 1 hour and about 6 hours, and wherein
the second heat treatment has a duration of between about 3 hours and about 15 hours and a temperature of between about 600° C. and about 900° C.
8. The method of claim 1 , wherein the recycled electrode material has a lithium concentration of at least about 99 wt %.
9. The method of claim 1 , further comprising:
washing the electrode material to remove at least a portion of the binder.
10. The method of claim 1 , further comprising:
prior to the first heat treatment, removing oxidizable impurities from the electrode material via treatment with at least one of an acid having a pH of no more than about 4 or a base having a pH of at least about 13.
11. The method of claim 1 , wherein the second heat treatment vaporizes all of the binder remaining in the electrode material.
12. The method of claim 1 , further comprising:
after the first heat treatment, adding a lithium salt to the electrode material.
13. A method of recycling a quantity of battery waste, the battery waste including an electrode material and a current collector, the electrode material including an active material and a binder, the method comprising:
applying a first heat treatment in an inert or reducing gas environment at a temperature of between about 400° C. and about 600° C. to the battery waste, the first heat treatment decomposing at least about 80 wt % of the binder;
separating the electrode material from the current collector;
after the first heat treatment, adding a lithium salt to the electrode material; and
applying a second heat treatment in an inert or a reducing gas environment at a temperature between about 400° C. and about 1,200° C. to the electrode material to produce a regenerated electrode material.
14. The method of claim 13 , further comprising:
applying a surface treatment to the electrode material to remove surface coatings and/or surface impurities from the electrode material.
15. The method of claim 14 , wherein the surface treatment includes applying a solvent to the electrode material.
16. The method of claim 15 , wherein the solvent includes at least one of citric acid, acetic acid, oxalic acid, ammonia, ammonium hydroxide, ammonium chloride, or chemical derivatives thereof.
17. The method of claim 13 , wherein
the electrode material includes at least one of LiCoO 2 , LiMn 2 O 4 , LiFe t M 1-t PO 4 , or LiNi a Mn b Co c A d O 2 , wherein
M includes a metal element; wherein
a+b+c+d=1; wherein
0<t<1; and wherein
A=Al, Zr, or Mg.
18. The method of claim 13 , wherein the first heat treatment has a duration of between about 1 hour and about 6 hours, and wherein
the second heat treatment has a duration of between about 1 hour and about 5 hours and a temperature of between about 450° C. and about 800° C.
19. The method of claim 13 , wherein the first heat treatment has a duration of between about 1 hour and about 6 hours, and wherein
the second heat treatment has a duration of between about 3 hours and about 15 hours and a temperature of between about 600° C. and about 900° C.
20. The method of claim 13 , further comprising:
washing the electrode material to remove at least a portion of the binder.
21. A method of recycling a quantity of battery waste, the battery waste including an electrode material and a current collector, the electrode material including an active material and a binder, the method comprising:
applying a first heat treatment at a temperature of between about 400° C. and about 600° C. to the battery waste in an inert or reducing gas environment, the first heat treatment decomposing at least about 80 wt % of the binder;
separating the electrode material from the current collector; and
applying a second heat treatment in an inert or a reducing gas environment at a temperature between about 400° C. and about 1,200° C. to the electrode material to produce a regenerated electrode material, the second heat treatment decomposing at least 90 wt % of binder remaining in the electrode material to produce a regenerated electrode material.
22. The method of claim 21 , further comprising:
applying a surface treatment to the electrode material to remove surface coatings and/or surface impurities from the electrode material.
23. The method of claim 22 , wherein the surface treatment includes applying a solvent to the electrode material.
24. The method of claim 21 , wherein
the electrode material includes at least one of LiCoO 2 , LiMn 2 O 4 , LiFe t M 1-t PO 4 , or LiNi a Mn b Co c A d O 2 , wherein
M includes a metal element; wherein
a+b+c+d=1; wherein
0<t<1; and wherein
A=Al, Zr, or Mg.
25. The method of claim 21 , further comprising:
washing the electrode material to remove at least a portion of the binder.
26. The method of claim 21 , wherein the recycled electrode material has a lithium concentration of at least about 99 wt %.
27. The method of claim 22 , further comprising:
prior to the first heat treatment, removing oxidizable impurities from the electrode material via treatment with at least one of an acid having a pH of no more than about 4 or a base having a pH of at least about 13.