1 . A method for forming an oxidation protection system on a carbon-carbon composite structure, comprising:

applying a barrier layer configured to bond with the carbon-carbon composite structure to the carbon-carbon composite structure;

applying a silicone-based slurry to the carbon-carbon composite structure, the silicone-based slurry including metal pigments disposed therein;

baking the applied silicone-based slurry in an inert atmosphere to form a microporous structure;

applying a sealing slurry comprising a silicon compound, a glass mixture, a glass former, a glass modifier, and a carrier fluid to the silicone-based slurry to provide a seal for the silicone-based slurry; and

heating the carbon-carbon composite structure.

2 . The method of claim 1 , wherein the glass mixture including a first glass compound and a second glass compound, the first glass compound having a first viscosity-temperature profile in which the viscosity of the first glass compound at given temperatures is at least two orders of magnitude smaller than the viscosity of the second glass compound having a second viscosity-temperature profile.

3 . The method of claim 1 , wherein the metal pigments include at least one of aluminum, silicon, chromium, iron, copper, nickel, silver, and gold.

4 . The method of claim 3 , wherein the metal pigments includes at least one of aluminum and silicon.

5 . The method of claim 1 , wherein the metal pigments are between 1% and 20% by weight of the silicone-based slurry.

6 . The method of claim 1 , wherein the metal pigments include a median diameter range between 0.5 μm and 70 μm.

7 . The method of claim 1 , wherein the metal pigments are leafing pigments, wherein the silicone-based slurry comprises one or more solvents, and wherein in response to the one or more solvents in the silicone-based slurry evaporating, convection currents push the metal pigments to a surface of a silicone-based coating formed from the silicone-based slurry from the heating of the carbon-carbon composite structure.

8 . The method of claim 1 , wherein the metal pigments are non-leafing pigments, and wherein in response to the heating of the carbon-carbon composite structure, the non-leafing pigments are distributed throughout a silicone-based coating formed from the silicone-based slurry.

9 . A carbon-carbon composite component, comprising:

a carbon-carbon composite structure; and

an oxidation protection system disposed on the carbon-carbon composite structure, the oxidation protection system including:

a barrier layer bonded to the carbon-carbon composite structure;

a primary layer coupled to the composite structure, the primary layer including a silicone-based coating with metal pigments baked into a microporous framework; and

a sealing layer comprising a silicon compound, a glass mixture, a glass former, a glass modifier, and a carrier fluid applied to the primary layer to provide a seal coating for the silicone-based coating, the sealing layer configured to penetrate a microporous framework of the primary layer.

10 . The carbon-carbon composite component of claim 9 , wherein the metal pigments comprise leafing metal pigments.

11 . The carbon-carbon composite component of claim 10 , wherein the leafing metal pigments form a leafing layer between the primary layer and the sealing layer.

12 . The carbon-carbon composite component of claim 9 , wherein the metal pigments comprise non-leafing metal pigments distributed throughout the silicone-based coating.

13 . The carbon-carbon composite component of claim 9 , wherein the metal pigments include a median diameter range between 0.5 μm and 70 μm.

14 . The carbon-carbon composite component of claim 9 , wherein the metal pigments are between 1% and 20% by weight of the silicone-based coating.

15 . The carbon-carbon composite component of claim 9 , wherein the metal pigments comprise at least one of aluminum, silicon, chromium, iron, copper, nickel, silver, and gold.

16 . An oxidation protection system for a carbon-carbon composite structure, the oxidation protection system comprising:

a silicone-based coating configured to couple to the carbon-carbon composite structure, the silicone-based coating including metal pigments; and

a sealing layer configured to couple to the silicone-based coating, the sealing layer configured to penetrate a microporous framework formed from the silicone-based coating, the sealing layer formed from a glass mixture including a first glass compound and a second glass compound, the first glass compound having a first viscosity-temperature profile that is at least two orders of magnitude below a second viscosity-temperature profile of the second glass compound.

17 . The oxidation protection system of claim 16 , wherein the metal pigments are leafing metal pigments, and wherein, the leafing metal pigments form a leafing layer between the silicone-based coating and the sealing layer.

18 . The oxidation protection system of claim 16 , wherein the metal pigments are non-leafing metal pigments, and wherein the metal pigments are distributed throughout the silicone-based coating.

19 . The oxidation protection system of claim 16 , wherein the metal pigments comprise at least one of aluminum, silicon, chromium, iron, copper, nickel, silver, and gold.