Granted Patent B2

US 12,573,674 · App. 17/622,508 · Granted Mar 10, 2026

Inventors: Young Jae Kim (Daejeon, KR); Jung Woo Yoo (Daejeon, KR)

Assignee: LG ENERGY SOLUTION, LTD.

H01M10/446H01M4/0404H01M4/505H01M4/525H01M10/0468H01M10/0525H01M2004/021H01M2004/027H01M2004/028

Abstract

Claims (27)

1 . A method of manufacturing a secondary battery, comprising:

forming a secondary battery structure comprising an electrode assembly comprising a negative electrode, a positive electrode, and a separator, and an electrolyte solution; and

activating the secondary battery structure by charging and discharging for at least one cycle while pressing the secondary battery structure at 1.5 MPa to 3.5 MPa,

wherein the negative electrode comprises a silicon-based active material,

wherein the secondary battery structure has an N/P ratio of 1.5 to 4, wherein the N/P ratio is calculated by Equation 1 below,

N/P ratio=discharge capacity per unit area of negative electrode/discharge capacity per unit area of positive electrode,  [Equation 1]

wherein a porosity of the negative electrode before activation is in a range of 37% to 45%,

wherein the negative electrode comprises a negative electrode current collector and a negative electrode active material layer formed on the negative electrode current collector,

the negative electrode active material layer comprises the silicon-based active material, and

a porosity of the negative electrode after activation calculated by Equation 3 below is in a range of 55% to 70%,

porosity of negative electrode after activation (%)=[1−{(electrode density of negative electrode active material layer before activation× d 1 /d 2 )/(true density of negative electrode active material layer before activation)}]×100  [Equation 3]

where,

d 1 is a thickness of a negative electrode active material layer before activation,

d 2 is a thickness of a negative electrode active material layer after activation,

an electrode density of the negative electrode active material layer before activation is the density of a negative electrode active material layer measured with the negative electrode before activation, and

a true density of the negative electrode active material layer before activation is the density of the negative electrode active material layer measured when the negative electrode before activation is pressed with pressing equipment until a thickness of the negative electrode does not change.

2 . The method of claim 1 , wherein in the activating the secondary battery structure, the pressing is performed at 2 MPa to 3 MPa.

3 . The method of claim 1 , wherein the silicon-based active material comprises a compound represented by Formula 1 below,

SiO x (0 ≤x< 2).  [Formula 1]

4 . The method of claim 1 , wherein the silicon-based active material is Si.

5 . The method of claim 1 , wherein an average particle diameter (D 50 ) of the silicon-based active material is in a range of 1 μm to 10 μm.

6 . The method of claim 1 , wherein the activating the secondary battery structure is performed by disposing the secondary battery structure between a pair of pressing plates and then pressing the secondary battery structure at 25 kgf·cm to 55 kgf·cm.

7 . The method of claim 1 , wherein the activating the secondary battery structure is performed at 23° C. to 27° C.

8 . The method of claim 1 , wherein in the activating the secondary battery structure, the charging and discharging are performed for 2 cycles to 8 cycles.

9 . The method of claim 1 , wherein

the positive electrode comprises a positive electrode current collector and a positive electrode active material containing a lithium-nickel-cobalt-manganese-based composite oxide formed on the positive electrode current collector, and

in the activating the secondary battery structure, the charging and discharging are performed in a voltage range of 2.5 V to 4.2 V.