Multi-step process for forming a barrier film for use in copper layer formation
View Patent ↗Embodiments of the invention include a method for forming a copper interconnect having a bi-layer copper barrier layer. The method comprises the steps of providing a substrate with a low-K dielectric insulating layer and an opening in the insulating layer. A first barrier layer of tantalum/tantalum nitride is formed on the insulating layer and in the opening. A second barrier layer consisting of a material selected from the group of palladium, chromium, tantalum, magnesium, and molybdenum is formed on the first barrier layer. A copper seed layer is formed on the second barrier layer and implanted with barrier ions and a bulk copper layer is formed on the seed layer. The substrate is annealed and subject to further processing which can include planarization.
1. A method for forming a copper interconnect having a robust copper barrier layer, the method comprising:
providing a substrate having an insulating layer and an opening in the insulating layer configured to receive an inlaid conducting structure;
forming at least two barrier layers on the insulating layer and in the opening, wherein the two barrier layers include a first barrier layer having a second barrier layer formed thereon wherein each of the barrier layers are fabricated so each have a different material composition wherein the second barrier layer consists of a material selected from the group: palladium, magnesium, and molybdenum;
forming a copper seed layer on the second barrier layer;
implanting the seed layer with barrier material ions to form an implanted seed layer;
forming a bulk copper containing layer on the implanted seed layer; and
annealing the substrate, so that the barrier material ions migrate through the seed layer to the interface between the second barrier layer and the copper seed layer to form a final barrier layer.
2. The method of claim 1 , wherein the opening is a trench.
3. The method of claim 1 , wherein the opening is a combination of a trench overlying a via.
4. The method of claim 1 wherein barrier materials of the second barrier layer further consist of a material selected from the group: chromium and tantalum.
5. The method of claim 1 wherein barrier materials of the second barrier layer further consist of a vanadium material.
6. The method of claim 1 wherein barrier materials of the second barrier layer further consist of a tungsten material.