Polytetrafluoroethylene dispersion for electroless nickel plating applications
View Patent ↗A low viscosity silicone glycol surfactant together with glycerin is added to a polytetrafluoroethylene dispersion for use with an electroless nickel plating bath. The improved plating bath produces a stable PTFE dispersion that continues to work as the plating bath ages and that produces an electroless nickel deposit with greater than 20 percent by volume of PTFE in the deposit.
1. An aqueous polytetrafluoroethylene dispersion comprising a low viscosity silicone glycol surfactant and polytetrafluoroethylene powder.
2. A polytetrafluoroethylene dispersion according to claim 1 , wherein the dispersion also comprising at least one material selected from the group consisting of cationic wetting agents, non-ionic wetting agents, and combinations thereof.
3. A polytetrafluoroethylene dispersion according to claim 2 , wherein said cationic wetting agent is present in the dispersion in an amount of about 10-15 grams/1000 grams of dispersion.
4. A polytetrafluoroethylene dispersion according to claim 2 , wherein said non-ionic wetting agent is present in the dispersion in an amount of about 5-15 grams/1000 grams of dispersion.
5. A polytetrafluoroethylene dispersion according to claim 2 , wherein at least one of said cationic wetting agent and said non-ionic wetting agent comprises a fluorocarbon wetting agent.
6. A polytetrafluoroethylene dispersion according to claim 1 , wherein said silicon glycol surfactant is present in the dispersion in an amount of about 1-10 grams/1000 grams of dispersion.
7. A polytetrafluoroethylene dispersion according to claim 1 wherein the dispersion also comprises glycerine.
8. A polytetrafluoroethylene dispersion according to claim 1 , wherein said polytetrafluoroethylene powder is present in said dispersion in an amount of about 500-700 grams/1000 grams of dispersion.
9. A polytetrafluoroethylene dispersion according to claim 1 , wherein said low viscosity silicone glycol surfactant has a viscosity of about 30-60 centistokes.
10. A polytetrafluoroethylene dispersion according to claim 9 , wherein said low viscosity silicone glycol surfactant has a viscosity of about 40-50 centistokes.
11. A polytetrafluoroethylene dispersion according to claim 1 , wherein said polytetrafluoroethylene powder has a nominal particle size of about 350 to 450 nanometers.
12. A polytetrafluoroethylene dispersion according to claim 11 , wherein said polytetrafluoroethylene powder has a nominal particle size of about 400 nanometers.
13. An improved electroless nickel composite plating bath comprising:
a) a source of nickel ions;
b) a hypophosphite compound;
c) a pH adjusting compound;
d) a complexing agent for the nickel ions; and
e) a polytetrafluoroethylene dispersion comprising:
i) a low viscosity silicone glycol surfactant; and
ii) polytetrafluoroethylene powder.
14. An improved electroless nickel composite plating bath according to claim 13 , wherein the dispersion also comprises at least one material selected from the group consisting of cationic wetting agents, and non-ionic wetting agents, and combinations thereof.
15. An improved electroless nickel composite plating bath according to claim 14 , wherein said cationic wetting agent is present in the dispersion in an amount of about 10-15 grams/1000 grams of dispersion.
16. An improved electroless nickel composite plating bath according to claim 14 , wherein said non-ionic wetting agent is present in the dispersion in an amount of about 5-15 grams/1000 grams of dispersion.
17. An improved electroless nickel composite plating bath according to claim 14 , wherein at least one of said cationic wetting agent and said non-ionic wetting agent comprises a fluorocarbon wetting agent.
18. An improved electroless nickel composite plating bath according to claim 13 , wherein said silicon glycol surfactant is present in the dispersion in an amount of about 1-10 grams/1000 grams of dispersion.
19. An improved electroless nickel composite plating bath according to claim 13 wherein the dispersion also comprises glycerine.
20. An improved electroless nickel composite plating bath according to claim 13 , wherein said polytetrafluoroethylene powder is present in said dispersion in an amount of about 500-700 grams/1000 grams of dispersion.
21. An improved electroless nickel composite plating bath according to claim 13 , wherein said low viscosity silicone glycol surfactant has a viscosity of about 30-60 centistokes.
22. An improved electroless nickel composite plating bath according to claim 21 , wherein said low viscosity silicone glycol surfactant has a viscosity of about 40-50 centistokes.
23. An improved electroless nickel composite plating bath according to claim 13 , wherein said polytetrafluoroethylene powder has a nominal particle size of about 350 to 450 nanometers.
24. An improved electroless nickel composite plating bath according to claim 23 , wherein said polytetrafluoroethylene powder has a nominal particle size of about 400 nanometers.
25. An improved electroless nickel composite plating bath according to claim 13 , wherein said polytetrafluoroethylene dispersion is present in said plating bath in an amount of about 2-12 milliliters per liter of plating bath.
26. An improved electroless nickel composite plating bath according to claim 13 , wherein said pH adjusting compound is ammonia and the pH of said plating bath is about 4.9 to 5.0.