Glass ceramics, chemically strengthened glass, and semiconductor substrate
A glass sheet, containing, in mass % on an oxide basis: 45-70% of SiO 2 , 1-15% of Al 2 O 3 , 10-25% of Li 2 O, 0-10% of Na 2 O, 0-5% of K 2 O, and 0-15% of ZrO 2 . K 2 O/R 2 O is 0.10 or less and ZrO 2 /R 2 O is 0.30 or more, where R 2 O is a total content of Li 2 O, Na 2 O, and K 2 O. The glass sheet has an average thermal expansion coefficient at 50° C.-350° C. of 90×10 −7 /° C.-140×10 −7 /° C. and a Young's modulus of 85 GPa or more.
1. A glass sheet, comprising:
a glass comprising lithiumphosphate crystals and having a composition comprising, in mass % on an oxide basis, 45-64% of SiO 2 , 8-15% of Al 2 O 3 , 10-25% of Li 2 O, 1.9-10% of Na 2 O, 0-5% of K 2 O, 4-5.7% of P 2 O 5 , and 6-15% of ZrO 2 such that K 2 O/R 2 O is 0 to 0.10, and ZrO 2 /R 2 O is 0.30 to 1.5, where R 2 O is a total content of Li 2 O, Na 2 O, and K 2 O,
wherein the glass has an average thermal expansion coefficient in a range of 90×10 −7 /° C. to 140×10 −7 /° C. at 50° C. to 350° C. and a Young's modulus of 92 GPa or more.
2. The glass sheet according to claim 1 , wherein the composition of the glass comprises, in mass % on an oxide basis, 50-64% of SiO 2 , 8-10% of Al 2 O 3 , 10-20% of Li 2 O, 1.9-7% of Na 2 O, 0-3% of K 2 O, 5.7% of P 2 O 5 , 6-11% of ZrO 2 , and 1-5% of Y 2 O 3 .
3. The glass sheet according to claim 2 , wherein a total content of BaO, SrO, MgO, CaO, and ZnO in the composition of the glass is 2% or more.
4. The glass sheet according to claim 1 , wherein the composition of the glass comprises a coloring component comprising at least one oxide selected from the group consisting of Co 3 O 4 , MnO 2 , Fe 2 O 3 , NiO, CuO, Cr 2 O 3 , V 2 O 5 , Bi 2 O 3 , SeO 2 , Er 2 O 3 , and Nd 2 O 3 .
5. The glass sheet according to claim 4 , wherein a content of the coloring component in the composition of the glass is 1% or less in total in mass % on an oxide basis.
6. A semiconductor-supporting substrate, comprising:
the glass sheet of claim 1 .
7. The glass sheet according to claim 1 , wherein the glass comprises lithium metasilicate crystals.
8. The glass sheet according to claim 7 , wherein the glass does not comprise lithium disilicate.
9. The glass sheet according to claim 1 , wherein the glass has a light transmittance in a range of 85% to 91% when the glass has a thickness of 0.7 mm.
10. The glass sheet according to claim 1 , wherein the glass has a haze value in a range of 0.02% to 1.0% when the glass has a thickness of 0.7 mm.
11. The glass sheet according to claim 1 , wherein the glass has a degree of crystallinity in a range of 5% to 70%.
12. The glass sheet according to claim 11 , wherein the glass comprises precipitated crystals having an average particle size of 80 nm or less.
13. The glass sheet according to claim 1 , wherein the glass has a Vickers hardness of 600 or more.
14. The glass sheet according to claim 1 , wherein the glass has a glass transition temperature in arrange of 390° C. to 650° C.
15. The glass sheet according to claim 2 , wherein the composition of the glass comprises a coloring component comprising at least one oxide selected from the group consisting of Co 3 O 4 , MnO 2 , Fe 2 O 3 , NiO, CuO, Cr 2 O 3 , V 2 O 5 , Bi 2 O 3 , SeO 2 , Er 2 O 3 , and Nd 2 O 3 .
16. The glass sheet according to claim 15 , wherein a content of the coloring component in the composition of the glass is 1% or less in total in mass % on an oxide basis.
17. A semiconductor-supporting substrate, comprising:
the glass sheet of claim 2 .
18. The glass sheet according to claim 2 , wherein the glass comprises lithium metasilicate crystals.
19. The glass sheet according to claim 18 , wherein the glass does not comprise lithium disilicate.
20. The glass sheet according to claim 2 , wherein the glass has a light transmittance in a range of 85% to 91% when the glass has a thickness of 0.7 mm.