Multilayer body and electronic component formed of same
A laminate body including a base material and a flat silicone sealing layer adhered thereto, generally without any voids, is provided. Also provided is a curable hot melt silicone composition layer with a particular curable hot melt silicone composition, providing a laminate body that does not readily cause stress on a substrate after the curable hot melt silicone composition is cured. A laminate body comprises a base material, and a curable hot melt silicone composition layer in contact with the base material. The curable hot melt silicone composition includes an organopolysiloxane resin containing siloxane units selected from a group containing T units or Q units making up at least 20 mol % or more of all siloxane units. The curable hot melt silicone composition generally has a melt viscosity as measured using a flow tester at a pressure of 2.5 MPa and at 100° C. of 5,000 Pa·s or less.
1 . A laminate body, comprising:
a base material; and
a curable hot melt silicone composition layer in contact with the base material;
wherein the curable hot melt silicone composition includes an organopolysiloxane resin containing a siloxane unit selected from a group including a siloxane unit expressed by R 1 SiO 3/2 where R 1 indicates an independent substituted or unsubstituted alkyl group or substituted or unsubstituted aryl group, and a siloxane unit expressed as SiO 4/2 making up at least 20 mol % or more of all siloxane units;
wherein the melt viscosity of the curable hot melt silicone composition as measured by a flow tester at a pressure of 2.5 MPa at 100° C. is 500 Pa·s or less;
wherein the curable hot melt silicone composition includes at least:
(A) an organopolysiloxane resin containing a siloxane unit expressed by SiO 4/2 making up at least 20 mol % or more of all siloxane units, and
(B) a straight or branched chain organopolysiloxane that is liquid or has plasticity at 25° C.; and
wherein component (A) comprises:
(A1′) an organopolysiloxane resin containing a curing reactive functional group including a carbon-carbon double bond in the molecule and containing a siloxane unit expressed by SiO 4/2 making up at least 20 mol % of all siloxane units, that does not independently have hot-melt properties and is solid at 25° C.; and
(A2′) an organopolysiloxane resin that does not have a curing reactive functional group containing a carbon-carbon double bond in the molecule while containing a siloxane unit expressed by SiO 4/2 making up at least 20 mol % or more of all siloxane units, that does not independently have hot-melt characteristics and is solid at 25° C.
2 . The laminate body according to claim 1 , wherein the base material is a first base material, and the surface of the curable hot melt silicone composition layer on an opposite side of the surface in contact with the first base material is in contact with a second base material and the curable hot melt silicone composition layer is interposed between the first base material and the second base material.
3 . The laminate body according to claim 1 , wherein the curable hot melt silicone composition layer includes one or more layers, and when there are two or more layers, the compositions of the curable hot melt silicone compositions of each of the two or more layers are mutually different.
4 . The laminate body according to claim 1 , wherein the laminate body only includes one base material or the laminate body includes a first base material, a second base material, and a curable hot melt silicone composition layer interposed therebetween, one or both of the base materials is a substrate that is an electronic component or a semiconductor precursor.
5 . The laminate body according to claim 4 , wherein;
the laminate body includes the first base material, the second base material, and the curable hot melt silicone composition layer interposed therebetween,
the first base material is an electronic component or a semiconductor precursor, and
the second base material is a release film.
6 . The laminate body according to claim 4 , wherein;
the laminate body includes the first base material, the second base material, and the curable hot melt silicone composition layer interposed therebetween,
the first base material and the second base material are both an electronic component or a semiconductor precursor.
7 . The laminate body according to claim 1 , wherein the R 1 of R 1 SiO 3/2 is an aryl group.
8 . The laminate body according to claim 1 , wherein the melt viscosity of the curable hot melt silicone composition at a shear rate of 1s −1 and 100° C. is 5,000 Pa·s or lower and the melt viscosity as measured using a flow tester at 2.5 MPa and 100° C. is 140 Pa·s or lower.
9 . The laminate body according to claim 1 , wherein when cured, the curable hot melt silicone composition forms a cured product with a tan δ, which is the ratio of the storage elastic modulus and the loss elastic modulus, of 0.05 or more over a temperature range that spans over 100° C. or more within a range of −50° C. to 200° C.
10 . The laminate body according to claim 1 , wherein, when cured, the curable hot melt silicone composition forms a cured product with a shore A hardness of 40 or more.
11 . The laminate body according to claim 1 , manufactured using any one of manufacturing methods of compression molding, press molding, or vacuum lamination.
12 . The laminate body according to claim 1 , wherein the curable hot melt silicone composition is free of M 4 Q silicone, where M represents a (R 1 3 SiQ 1/2 ) unit, Q represents a (SiO 4/2 ) unit, and R 1 indicates an independent substituted or unsubstituted alkyl group or substituted or unsubstituted aryl group.
13 . The laminate body according to claim 1 , including the multilayer laminate structure containing the curable hot melt silicone composition layer and a functional layer in contact with one of the surfaces of the curable hot melt silicone composition layer;
optionally, wherein the functional layer includes a curable hot melt silicone composition with a composition different from the curable hot melt silicone composition that enables imparting functionality that the composition included in the curable hot melt silicone composition layer or the cured product resulting therefrom does not have, to the multilayer laminate body or imparting functionality that is insufficient in the composition included in the curable hot melt silicone composition layer or the cured product resulting therefrom; and/or
optionally, wherein the functional layer is a layer selected from a group including a layer containing a material with lower tack than the curable hot melt silicone composition, a layer containing a material with a higher elastic modulus than the cured product formed by curing the curable hot melt silicone composition, a layer containing a curable material with an elastic modulus that will be higher than that of the cured product formed by curing the curable hot melt silicone composition, a layer containing a material having water repellency and/or oil repellency, and an optical functional layer.
14 . A peelable laminate body, comprising:
a multilayer laminate structure including the curable hot melt silicone composition layer according to claim 13 and the functional layer in contact with a surface of the layer;
wherein the multilayer laminate structure is further provided with a release film or protective film adhered to one of either of the two outermost surfaces thereof.
15 . A laminate body, comprising:
a multilayer laminate structure including the curable hot melt silicone composition layer according to claim 13 and the functional layer in contact with a surface of the layer;
wherein the structure of the laminate body is provided with a base material without peeling properties laminated on the surface of the curable hot melt silicone composition layer that is not in contact with the functional layer.
16 . A laminate body, comprising a cured silicone layer obtained from curing the curable hot melt silicone composition contained in the laminate body according to claim 1 , optionally wherein the laminate body is an electronic component.
17 . A laminate body including one base material and a curable hot melt silicone composition layer in contact with the base material according to claim 1 , manufactured using a method including the following steps:
1 arranging a sheet or film containing the curable hot melt silicone composition in a reduced-pressure chamber with respect to the base material arranged in the chamber such that the sheet or film can be caused to come into contact with the base material in a subsequent step; a step in a reduced-pressure chamber of placing a sheet or film containing the curable hot melt silicone composition on the base material arranged in the chamber; or a step of setting the base material with a sheet or film containing the curable hot melt silicone composition placed so as to contact the base material beforehand in a reduced-pressure chamber;
2 depressurizing in the reduced-pressure chamber to a prescribed pressure;
3 heating inside the reduced-pressure chamber at reduced pressure to melt the curable hot melt silicone composition sheet or film and adhere it to the base material and, as needed, press one or both of the base material and sheet or film, after adhering, to pressure bond the curable hot melt silicone composition sheet or film to the base material; and
4 canceling the pressure reduction inside the reduced-pressure chamber and removing the laminate body including a layer containing the curable hot melt silicone composition, a cured layer thereof, a layer selected from a group containing half-cured layers, and the base material in contact with this layer from the chamber.
18 . A laminate body having a structure of two of the same or different base materials with the curable hot melt silicone composition layer interposed therebetween, obtained according to the method of claim 17 , wherein having a sheet or film containing the curable hot melt silicone composition arranged to enable coming into contact with the base material in a subsequent step or that is placed on the substrate beforehand, regarding the surface other than the surface that will come into contact with the base material at a subsequent step or the surface in contact with the base material, a base material that is the same or different from the base material is arranged so as to enable coming into contact with the sheet or film containing the curable hot melt silicone composition at a subsequent step or regarding this other surface, a base material that is the same or different from the base material is placed in contact with the sheet or film containing the curable hot melt silicone composition beforehand.
19 . The laminate body obtained according to the method of claim 17 , including:
two of the same or different base materials with a the curable hot melt silicone composition layer interposed therebetween manufactured by;
laminating the curable hot melt silicone composition layer derived from a sheet or film containing the curable hot melt silicone layer on one surface of the base material, and
similar to steps 1) to 4), laminating the same or different base material as the base material onto the outer surface of the side of the base material not in contact with the curable hot melt silicone composition layer.
20 . The laminate body obtained according to the method of claim 17 , wherein the temperature for pressure bonding the curable hot melt silicone composition sheet or film to the base material is 50° C. or higher.