Metal-on-metal deposition methods for filling a gap feature on a substrate surface
Molybdenum (Mo) metal-on-metal (MoM) deposition methods for providing true bottom-up fill in vias and/or other gap features in device structures. These device structures contain metal at the bottom surface and have dielectric sidewalls. The deposition process provides molybdenum growth only, in some cases, on the metal film/layer to provide a selective process that can be called a metal-on-metal (MoM) process. The Mo MoM deposition process described herein are not limited to thin films (e.g., films less than 50 Å) and can be used to deposit thicker films (e.g., greater than 50 Å in some cases and greater than 200 Å in other useful cases) on metal surfaces while no, or substantially no, deposition is found on dielectric surfaces.
1 . A method for filling a gap feature on a substrate surface, comprising:
providing a substrate with a surface comprising a gap feature in a reaction chamber, wherein the gap feature includes a dielectric sidewall and a metal base;
partially filling the gap feature with a molybdenum film with a cyclical chemical vapor deposition (cyclical CVD) process, wherein the molybdenum film is selectively deposited on the metal base and wherein a cycle of the cyclical chemical vapor deposition process comprises:
providing a molybdenum precursor comprising one or more of MoCl 5 and MoCl 4 in the reaction chamber; and
providing a reactant in the reaction chamber to form a layer of the molybdenum film; and
repeating the partially filling the gap step until the molybdenum film has at least a predefined thickness.
2 . The method of claim 1 , wherein the metal base comprises a metal selected from the group consisting of tungsten (W), titanium nitride (TiN), ruthenium (Ru), cobalt (Co), and copper (Cu).
3 . The method of claim 1 , wherein the reactant is a reducing agent.
4 . The method of claim 1 , wherein a thickness of molybdenum grown on the dielectric surface is substantially 0 Å.
5 . The method of claim 1 , wherein the molybdenum precursor comprises MoCl 4 .
6 . The method of claim 1 , wherein the molybdenum precursor is MoCl 4 .
7 . The method of claim 1 , wherein the reactant is continuously provided during the cycle of the cyclical chemical vapor deposition process.
8 . The method of claim 7 , further comprising heating the substrate to a substrate temperature in the range of 350 to 450° C. and maintaining the reaction chamber at a pressure in the range of 10 to 100 Torr during the partially filling the gap step.
9 . The method of claim 7 , wherein the reactant consists of hydrogen (H 2 ).
10 . The method of claim 1 , wherein the predefined thickness is greater than 50 Å and wherein the molybdenum film selectively grows on the metal film relative to the dielectric sidewall for at least the predefined thickness.
11 . The method of claim 1 , wherein the predefined thickness is in the range of 20 to 600 Å and wherein the molybdenum film selectively grows on the metal film relative to the dielectric sidewall for at least the predefined thickness.
12 . A method of bottom-up filling a gap feature on a surface of a substrate, comprising
surface cleaning a substrate with a gap feature having sidewalls with dielectric surface and a bottom surface with a metal film to remove metal oxides from the metal film;
after the surface cleaning, providing the substrate in a reaction chamber;
heating the substrate to a substrate temperature greater than 350° C.;
contacting the substrate with a molybdenum precursor comprising one or more of MoCl 5 and MoCl 4 by periodically pulsing the molybdenum precursor;
contacting the substrate with a reducing agent, wherein contacting the substrate with the reducing agent comprises continuously providing the reducing agent during the step of contacting the substrate with the molybdenum precursor; and
repeating the contacting steps until a molybdenum film is formed on the metal film on the bottom surface of the gap feature, wherein the molybdenum film is formed with a selectivity of at least 50:1 between the metal film and the dielectric surface.
13 . The method of claim 12 , wherein the molybdenum film has a thickness of at least 200 Å.
14 . The method of claim 12 , wherein the metal film comprises a metal selected from the group consisting of W, TiN, Ru, Co, and Cu.
15 . The method of claim 12 , wherein the molybdenum precursor comprises MoCl 5 and wherein the substrate temperature is in the range of 350 to 550° C.
16 . The method of claim 12 , wherein the molybdenum precursor comprises MoCl 4 .
17 . A method for selectively depositing a molybdenum film on a semiconductor device structure, comprising:
providing a device structure in a reaction chamber, wherein the device structure comprises a substrate including a dielectric surface and a metal surface;
partially forming a molybdenum film selectively on the metal surface with a cyclical chemical vapor deposition (cyclical CVD) process, wherein a unit cycle of the cyclical chemical vapor deposition process comprises:
providing a molybdenum precursor in the reaction chamber;
purging the molybdenum precursor from the reaction chamber; and
providing a reactant in the reaction chamber, wherein the reactant comprises a reducing agent;
repeating the partially forming the molybdenum film step until the molybdenum film has a thickness greater than 200 Å and wherein a thickness of molybdenum grown on the dielectric surface is substantially 0 Å.
18 . The method of claim 17 , wherein the metal surface comprises a metal selected from the group consisting of W, TiN, Ru, Co, and Cu and wherein the molybdenum precursor is selected from the group consisting of MoCl 5 , MoCl 4 , MoO 2 Cl 2 , and MoOCl 4 .
19 . The method of claim 18 , wherein the method further comprises, prior to the partially forming the molybdenum film step, heating the substrate to a substrate temperature in the range of 350 to 550° C. when the molybdenum precursor comprises MoCl 5 or MoCl 4 and in the range of 350 to 450° C. when the molybdenum precursor comprises MoO 2 Cl 2 or MoOCl 4 .